Orgalloy® RS 6600 BLACK

Alternative and trade names
PA66
Want to keep this datasheet? Save it now in your required format

Description

Orgalloy® RS 6600 BLACK resin is a polyamide 66 alloy designed for injection molding. This black grade offers an outstanding dimensional stability, chemical resistance to automotive fluids and is ideal for the realization of complex parts.

This material data has been provided by Arkema High Performance Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.04 g/cm³

Show Supplier Material materials with Density of 1.04 g/cm³

ISO 1183

Moisture absorption

23.0 °C

1.2 %

Show Supplier Material materials with Moisture absorption of 1.2 %

Sim. to ISO 62

Water absorption

23.0 °C

2.9 %

Show Supplier Material materials with Water absorption of 2.9 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.33 GPa

Show Supplier Material materials with Elastic modulus of 2.33 GPa

ISO 527-1/-2

Elongation

23.0 °C

15 %

Show Supplier Material materials with Elongation of 15 %

ISO 527-1/-2, nominal

Elongation at yield

23.0 °C

6 %

Show Supplier Material materials with Elongation at yield of 6 %

ISO 527-1/-2

Hardness, Shore D

23.0 °C

76 [-]

Show Supplier Material materials with Hardness, Shore D of 76 [-]

ISO 7619-1, 15 seconds

Impact strength, Charpy notched

23.0 °C

7 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 7 kJ/m²

ISO 179/1eA

Yield strength

23.0 °C

55 MPa

Show Supplier Material materials with Yield strength of 55 MPa

ISO 527-1/-2

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

6.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 6.5E-5 1/K

ISO 11359-1/-2

Coefficient of thermal expansion, transverse

23.0 °C

1.1E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K

ISO 11359-1/-2

Heat deflection temperature, 0.45 MPa

160 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 160 °C

ISO 75-1/-2

Heat deflection temperature, 1.80 MPa

80 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 80 °C

ISO 75-1/-2

Melting point

255 °C

Show Supplier Material materials with Melting point of 255 °C

ISO 11357-1/-3, 10°C/min

Vicat softening temperature

170 °C

Show Supplier Material materials with Vicat softening temperature of 170 °C

ISO 306, 50°C/h 50N

Flammability

At thickness 1.6 mm IEC 60695-11-10: HB, At thickness 3.2 mm IEC 60695-11-10: HB and yellow card available

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Supplier Material materials with Comparative tracking index of 600 V

IEC 60112, Conditioned

Dielectric constant, 100Hz

23.0 °C

3 [-]

Show Supplier Material materials with Dielectric constant, 100Hz of 3 [-]

IEC 60250, Conditioned

Dielectric constant, 1MHz

23.0 °C

3 [-]

Show Supplier Material materials with Dielectric constant, 1MHz of 3 [-]

IEC 60250, Conditioned

Dielectric strength

23.0 °C

36 kV/mm

Show Supplier Material materials with Dielectric strength of 36 kV/mm

IEC 60243-1

Dissipation factor, 100Hz

23.0 °C

0.03 [-]

Show Supplier Material materials with Dissipation factor, 100Hz of 0.03 [-]

IEC 60250, Conditioned

Dissipation factor, 1MHz

23.0 °C

0.02 [-]

Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-]

IEC 60250, Conditioned

Volume resistivity

23.0 °C

1.00E+13 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+13 Ω·cm

min., IEC 60093, Conditioned

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

24 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 24 cm³/10min

ISO 1133, 275°C/2.16kg

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

ISO 294-4 2577

Shrinkage, transverse

23.0 °C

1.1 %

Show Supplier Material materials with Shrinkage, transverse of 1.1 %

ISO 294-4 2577

Technological properties

Property
Application areas

Main applications:

  • Electric connectors
  • Sport parts
  • Automotive fan shrouds

    or

    Fittings, Components, and Injection Molded Parts

  • Other

    Packaging:

  • This grade is delivered dried in sealed packaging (25kg bags) ready to be processed.

    Shelf life:

  • Two years from the date of delivery. For any use above this limit, please refer to our technical services.

  • Processing methods

    Injection Molding:

  • Drying time (only necessary for bags opened for more than two hours): 4-8 hours at 80°C
  • Injection temperature (min-recommended-max): 260-270-280°C
  • Mould temperature (min-max): 60-80°C