Pebax® 5533 SN 70 BLACK

Alternative and trade names
TPA-CD

Want to keep this datasheet? Save it now in your required format

Description

Pebax® 5533 SN 70 BLACK resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SN 70 grade is made conductive thanks to carbon black.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Condition	Testing Standard
Density	1.09 g/cm³ Show Supplier Material materials with Density of 1.09 g/cm³	dry	ISO 1183
Moisture absorption	0.5 % Show Supplier Material materials with Moisture absorption of 0.5 %		Sim. to ISO 62
Water absorption	1.2 % Show Supplier Material materials with Water absorption of 1.2 %		Sim. to ISO 62

Mechanical

Property	Value	Condition	Testing Standard	Comment
Elastic modulus	0.298 GPa Show Supplier Material materials with Elastic modulus of 0.298 GPa	cond.	ISO 527-1/-2
	0.305 GPa Show Supplier Material materials with Elastic modulus of 0.305 GPa	dry	ISO 527-1/-2
Elongation	50 % Show Supplier Material materials with Elongation of 50 %	cond., dry	ISO 527-1/-2	min. \| nominal
Elongation at yield	31 % Show Supplier Material materials with Elongation at yield of 31 %	dry	ISO 527-1/-2
	36 % Show Supplier Material materials with Elongation at yield of 36 %	cond.	ISO 527-1/-2
Hardness, Shore D	60 [-] Show Supplier Material materials with Hardness, Shore D of 60 [-]	dry	ISO 7619-1	15 seconds
Impact strength, Charpy notched	No Break at 23°C	cond.	ISO 179/1eA
Impact strength, Charpy unnotched	No Break at 23 and -30°C	cond.	ISO 179/1eU
Yield strength	12 MPa Show Supplier Material materials with Yield strength of 12 MPa	cond.	ISO 527-1/-2
	19 MPa Show Supplier Material materials with Yield strength of 19 MPa	dry	ISO 527-1/-2

Thermal

Property	Value	Condition	Testing Standard	Comment
Coefficient of thermal expansion	0.00022 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.00022 1/K	dry	ISO 11359-1/-2
Melting point	159 °C Show Supplier Material materials with Melting point of 159 °C	dry	ISO 11357-1/-3	10°C/min
Flammability	At thickness 1.6 mm IEC 60695-11-10: HB, At thickness 3.2 mm IEC 60695-11-10: HB

Electrical

Property	Value	Condition	Testing Standard
Surface resistivity	5500 Ω/sq Show Supplier Material materials with Surface resistivity of 5500 Ω/sq	cond.	IEC 60093
Volume resistivity	1.1e+07 Ω·cm Show Supplier Material materials with Volume resistivity of 1.1e+07 Ω·cm	dry	IEC 60093

Rheological Properties

Property	Value	Condition	Testing Standard	Comment
Melt volume-flow rate	5 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 5 cm³/10min	dry	ISO 1133	250°C/5kg

Technological properties

Property

Application areas

Alternative Fuel Systems - CNG, LPG, LNG Lines and Tanks,Underground Fuel Containment

Fillers

Carbon Black

Processing methods

Injection Molding:

Typical melt temperature (Min / Recommended / Max) : 200°C / 240°C / 270°C.

Typical mold temperature : 25 – 60°C.

Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 65-75°C.

Extrusion:

Typical melt temperature (Min / Recommended / Max) : 210°C / 220°C / 230°C.

Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 65-75°C.