Pebax® 6333 SP 01

Alternative and trade names
TPA

Want to keep this datasheet? Save it now in your required format

Description

Polyether block amide Pebax® 6333 SP 01 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SP grade has been developed to be heat and UV resistant.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Condition	Testing Standard
Abrasion resistance	55 mm³ Show Supplier Material materials with Abrasion resistance of 55 mm³	dry	ISO 4649
Density	1.01 g/cm³ Show Supplier Material materials with Density of 1.01 g/cm³	dry	ISO 1183
Limiting oxygen index	20 % Show Supplier Material materials with Limiting oxygen index of 20 %	dry	ISO 4589-1/-2
Moisture absorption	0.7 % Show Supplier Material materials with Moisture absorption of 0.7 %		Sim. to ISO 62
Water absorption	1.1 % Show Supplier Material materials with Water absorption of 1.1 %		Sim. to ISO 62

Mechanical

Property	Value	Testing Standard	Condition	Comment
Compression set	47 [-] Show Supplier Material materials with Compression set of 47 [-]	ISO 815		for 24h
Elastic modulus	0.285 GPa Show Supplier Material materials with Elastic modulus of 0.285 GPa	ISO 527-1/-2	cond.
	0.307 GPa Show Supplier Material materials with Elastic modulus of 0.307 GPa	ISO 527-1/-2	dry
Elongation	50 % Show Supplier Material materials with Elongation of 50 %	ISO 527-1/-2	cond., dry	min. \| nominal
Elongation at yield	22 % Show Supplier Material materials with Elongation at yield of 22 %	ISO 527-1/-2	cond., dry
Hardness, Shore D	58 [-] Show Supplier Material materials with Hardness, Shore D of 58 [-]	ISO 7619-1	dry	15 seconds
Impact strength, Charpy notched	No Break at 23°C	ISO 179/1eA	cond., dry
Impact strength, Charpy unnotched	No Break at 23 and -30°C	ISO 179/1eU	dry and cond.
Tear strength	127 kN/m Show Supplier Material materials with Tear strength of 127 kN/m	ISO 34-1
Yield strength	22 MPa Show Supplier Material materials with Yield strength of 22 MPa	ISO 527-1/-2	cond.
	23 MPa Show Supplier Material materials with Yield strength of 23 MPa	ISO 527-1/-2	dry

Thermal

Property	Value	Condition	Testing Standard	Comment
Coefficient of thermal expansion	0.00014 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.00014 1/K	dry	ISO 11359-1/-2
Melting point	169 °C Show Supplier Material materials with Melting point of 169 °C	dry	ISO 11357-1/-3	10°C/min
Vicat softening temperature	157 °C Show Supplier Material materials with Vicat softening temperature of 157 °C		ISO 306	50°C/h 50N
Flammability	At thickness 1.6 mm IEC 60695-11-10: HB and yellow card available

Electrical

Property	Value	Condition	Testing Standard	Frequency
Comparative tracking index	600 V Show Supplier Material materials with Comparative tracking index of 600 V	cond.	IEC 60112
Dielectric constant	4 [-] Show Supplier Material materials with Dielectric constant of 4 [-]	dry	IEC 60250	1MHz
	9 [-] Show Supplier Material materials with Dielectric constant of 9 [-]	dry	IEC 60250	100Hz
Dielectric strength	42.5 kV/mm Show Supplier Material materials with Dielectric strength of 42.5 kV/mm	dry	IEC 60243-1
Dissipation factor	0.0757 [-] Show Supplier Material materials with Dissipation factor of 0.0757 [-]	dry	IEC 60250	1MHz
	0.144 [-] Show Supplier Material materials with Dissipation factor of 0.144 [-]	dry	IEC 60250	100Hz
Surface resistivity	1e+13 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+13 Ω/sq	cond.	IEC 60093
Volume resistivity	9e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 9e+13 Ω·cm	dry	IEC 60093

Rheological Properties

Property	Value	Condition	Testing Standard	Comment
Density of melt	0.83 g/cm³ Show Supplier Material materials with Density of melt of 0.83 g/cm³
Shrinkage	1.2 % Show Supplier Material materials with Shrinkage of 1.2 %	dry	ISO 294-4
	1.4 % Show Supplier Material materials with Shrinkage of 1.4 %	dry	ISO 294-4	Transverse
Specific heat capacity melt	2800 J/(kg·K) Show Supplier Material materials with Specific heat capacity melt of 2800 J/(kg·K)
Thermal conductivity of melt	0.18 W/(m·K) Show Supplier Material materials with Thermal conductivity of melt of 0.18 W/(m·K)

Technological properties

Property

Application areas

Conveyor Belts and Pulleys,Pneumatic Tubing,Tubing and Hoses,Hook and Loop Fasteners,Footwear - Outsoles,Ski Boots,Sports Equipment

Certifications

Yellow Card

Processing methods

Injection Molding:

Typical melt temperature (Min / Recommended / Max) : 230°C / 260°C / 290°C.

Typical mold temperature : 25 – 60°C.

Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 65-75°C.

Extrusion:

Typical melt temperature (Min / Recommended / Max) : 210°C / 225°C / 240°C.

Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 65-75°C.