General
Property | Value | Condition | Testing Standard |
---|---|---|---|
Abrasion resistance | 41 mm³ Show Supplier Material materials with Abrasion resistance of 41 mm³ | dry | ISO 4649 |
Density | 1.01 g/cm³ Show Supplier Material materials with Density of 1.01 g/cm³ | dry | ISO 1183 |
Moisture absorption | 0.76 % Show Supplier Material materials with Moisture absorption of 0.76 % | Sim. to ISO 62 | |
Water absorption | 1.43 % Show Supplier Material materials with Water absorption of 1.43 % | Sim. to ISO 62 |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elastic modulus | 0.39 GPa Show Supplier Material materials with Elastic modulus of 0.39 GPa | cond. | ISO 527-1/-2 | ||
0.414 GPa Show Supplier Material materials with Elastic modulus of 0.414 GPa | dry | ISO 527-1/-2 | |||
Elongation | 50 % Show Supplier Material materials with Elongation of 50 % | cond., dry | ISO 527-1/-2 | min. | nominal | |
Elongation at yield | 20 % Show Supplier Material materials with Elongation at yield of 20 % | cond. | ISO 527-1/-2 | ||
22 % Show Supplier Material materials with Elongation at yield of 22 % | dry | ISO 527-1/-2 | |||
Hardness, Shore D | 61 [-] Show Supplier Material materials with Hardness, Shore D of 61 [-] | dry | ISO 7619-1 | 15 seconds | |
Impact strength, Charpy notched | -30 °C | 20 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 20 kJ/m² | cond. | ISO 179/1eA | |
23 °C | 120 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 120 kJ/m² | cond. | ISO 179/1eA | ||
Impact strength, Charpy unnotched | No Break at 23 and -30°C | cond. | ISO 179/1eU | ||
Yield strength | 22 MPa Show Supplier Material materials with Yield strength of 22 MPa | cond. | ISO 527-1/-2 |
Thermal
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Healthcare-Other,IV Bags,Medical Catheters | |
Certifications | USP Class VI | |
Processing methods | Injection Molding: Extrusion: |