Pebax® 7033 SP 01

Alternative and trade names
TPA
Want to keep this datasheet? Save it now in your required format

Description

Polyether block amide Pebax® 7033 SP 01 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SP grade has been developed to be heat and UV resistant.

This material data has been provided by Arkema Technical Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting Standard

Density

1.01 g/cm³

Show Supplier Material materials with Density of 1.01 g/cm³

dry

ISO 1183

Moisture absorption

0.7 %

Show Supplier Material materials with Moisture absorption of 0.7 %

Sim. to ISO 62

Water absorption

1.1 %

Show Supplier Material materials with Water absorption of 1.1 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

0.39 GPa

Show Supplier Material materials with Elastic modulus of 0.39 GPa

cond.

ISO 527-1/-2

0.414 GPa

Show Supplier Material materials with Elastic modulus of 0.414 GPa

dry

ISO 527-1/-2

Elongation

50 %

Show Supplier Material materials with Elongation of 50 %

cond., dry

ISO 527-1/-2

min. | nominal

Elongation at yield

20 %

Show Supplier Material materials with Elongation at yield of 20 %

cond.

ISO 527-1/-2

22 %

Show Supplier Material materials with Elongation at yield of 22 %

dry

ISO 527-1/-2

Hardness, Shore D

61 [-]

Show Supplier Material materials with Hardness, Shore D of 61 [-]

dry

ISO 7619-1

15 seconds

Impact strength, Charpy notched

-30 °C

20 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 20 kJ/m²

cond.

ISO 179/1eA

23 °C

120 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 120 kJ/m²

cond.

ISO 179/1eA

Impact strength, Charpy unnotched

No Break at 23 and -30°C

dry and cond.

ISO 179/1eU

Tear strength

149 kN/m

Show Supplier Material materials with Tear strength of 149 kN/m

ISO 34-1

Yield strength

26 MPa

Show Supplier Material materials with Yield strength of 26 MPa

cond.

ISO 527-1/-2

Thermal

PropertyValueConditionTesting StandardComment

Coefficient of thermal expansion

0.00016 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 0.00016 1/K

dry

ISO 11359-1/-2

Melting point

172 °C

Show Supplier Material materials with Melting point of 172 °C

dry

ISO 11357-1/-3

10°C/min

Vicat softening temperature

164 °C

Show Supplier Material materials with Vicat softening temperature of 164 °C

ISO 306

50°C/h 50N

Flammability

At thickness 1.6 mm IEC 60695-11-10: HB, At Thickness 3.1 mm IEC 60695-11-10: HB and yellow card available

Electrical

PropertyValueConditionTesting Standard

Comparative tracking index

600 V

Show Supplier Material materials with Comparative tracking index of 600 V

cond.

IEC 60112

Surface resistivity

4e+13 Ω/sq

Show Supplier Material materials with Surface resistivity of 4e+13 Ω/sq

cond.

IEC 60093

Rheological Properties

PropertyValueConditionTesting StandardComment

Density of melt

0.83 g/cm³

Show Supplier Material materials with Density of melt of 0.83 g/cm³

Shrinkage

1.2 %

Show Supplier Material materials with Shrinkage of 1.2 %

dry

ISO 294-4

1.5 %

Show Supplier Material materials with Shrinkage of 1.5 %

dry

ISO 294-4

Transverse

Specific heat capacity melt

2700 J/(kg·K)

Show Supplier Material materials with Specific heat capacity melt of 2700 J/(kg·K)

Thermal conductivity of melt

0.2 W/(m·K)

Show Supplier Material materials with Thermal conductivity of melt of 0.2 W/(m·K)

Technological properties

Property
Application areas

Textile - Others,Footwear - Outsoles,Ski Boots,Sports Equipment

Certifications

Yellow Card

Processing methods

Injection Molding:

  • Typical melt temperature (Min / Recommended / Max) : 230°C / 260°C / 290°C
  • Typical mold temperature : 25 – 60°C
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 5-7 hours at 70-80°C


    Extrusion:

  • Typical melt temperature (Min / Recommended / Max) : 220°C / 235°C / 250°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 5-7 hours at 70-80°C.