Pebax® Clear 1200

Alternative and trade names
TPA
Want to keep this datasheet? Save it now in your required format

Description

Pebax® Clear 1200 resin combines a high transparency level with the excellent performance of Pebax® thermoplastic elastomer resin.

Pebax® Clear 1200 resin is produced from a renewable source. The percentage of renewable carbon according to ASTM D6866 (calculated) is 90%.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting Standard

Bio-based content

90 %

Show Supplier Material materials with Bio-based content of 90 %

Density

1.03 g/cm³

Show Supplier Material materials with Density of 1.03 g/cm³

dry

ISO 1183

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

1.3 GPa

Show Supplier Material materials with Elastic modulus of 1.3 GPa

cond.

ISO 527-1/-2

Elongation

50 %

Show Supplier Material materials with Elongation of 50 %

cond.

ISO 527-1/-2

min. | nominal

Elongation at yield

5.1 %

Show Supplier Material materials with Elongation at yield of 5.1 %

cond.

ISO 527-1/-2

Hardness, Shore D

73 [-]

Show Supplier Material materials with Hardness, Shore D of 73 [-]

dry

ISO 7619-1

15 seconds

Impact strength, Charpy notched

-30 °C

12 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m²

cond.

ISO 179/1eA

23 °C

8 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 8 kJ/m²

cond.

ISO 179/1eA

Thermal

PropertyValueConditionTesting StandardComment

Melting point

180 °C

Show Supplier Material materials with Melting point of 180 °C

dry

ISO 11357-1/-3

10°C/min

Optical

PropertyValueTesting Standard

Luminous transmittance

80 [-]

Show Supplier Material materials with Luminous transmittance of 80 [-]

ISO 13468-1/2

Rheological Properties

PropertyValueConditionTesting StandardComment

Shrinkage

1 %

Show Supplier Material materials with Shrinkage of 1 %

dry

ISO 294-4

1.1 %

Show Supplier Material materials with Shrinkage of 1.1 %

dry

ISO 294-4

Transverse

Technological properties

Property
Application areas

Sports Equipment

Processing methods

Injection Molding:

  • Typical melt temperature (Min / Recommended / Max) : 250°C / 270°C / 290°C.
  • Typical mold temperature (mirror polish to get the optimum transparency) : 50–70°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80°C.