Pebax® MV 1074 SA 01

Alternative and trade names
TPA
Want to keep this datasheet? Save it now in your required format

Description

Polyether block amide Pebax® MV 1074 SA 01 resin is a thermoplastic elastomer made of flexible and hydrophilic polyether and rigid polyamide.

Pebax® MV 1074 SA 01 resin is also an inherently dissipative polymer and can be dry blended or compounded with a polymer matrix to lower the surface resistivity of the final part. This hydrophilic grade when extruded into either a thin film or laminated on to a substrate offers excellent permeability to moisture vapor while remaining waterproof . This SA grade is specially designed to food uses. Refractive index according to an internal method is 1.502.

This material data has been provided by Arkema High Performance Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.07 g/cm³

Show Supplier Material materials with Density of 1.07 g/cm³

ISO 1183

Limiting oxygen index

23.0 °C

19 %

Show Supplier Material materials with Limiting oxygen index of 19 %

ISO 4589-1/-2

Moisture absorption

23.0 °C

1.4 %

Show Supplier Material materials with Moisture absorption of 1.4 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

0.1 GPa

Show Supplier Material materials with Elastic modulus of 0.1 GPa

ISO 527-1/-2

Elongation

23.0 °C

50 - 500 %

Show Supplier Material materials with Elongation of 50 - 500 %

min: ISO 527-1/-2, max: ISO 527-3

Elongation, transverse

23.0 °C

700 %

Show Supplier Material materials with Elongation, transverse of 700 %

ISO 527-3

Hardness, Shore D

23.0 °C

40 [-]

Show Supplier Material materials with Hardness, Shore D of 40 [-]

ISO 7619-1, 15 seconds

Tensile strength

23.0 °C

32 MPa

Show Supplier Material materials with Tensile strength of 32 MPa

ISO 527-3

Tensile strength, transverse

23.0 °C

34 MPa

Show Supplier Material materials with Tensile strength, transverse of 34 MPa

ISO 527-3

Impact strength, Charpy notched

No break @ 23,-30°C, ISO 179/1eA

Impact strength, Charpy unnotched

No break @ 23,-30°C, ISO 179/1eU

Thermal

PropertyValueComment

Glass transition temperature

-40 °C

Show Supplier Material materials with Glass transition temperature of -40 °C

ISO 11357-1/-2, 10°C/min

Melting point

158 °C

Show Supplier Material materials with Melting point of 158 °C

ISO 11357-1/-3, 10°C/min

Electrical

PropertyTemperatureValueComment

Dielectric strength

23.0 °C

5 kV/mm

Show Supplier Material materials with Dielectric strength of 5 kV/mm

IEC 60243-1

Volume resistivity

23.0 °C

1.50E+11 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.50E+11 Ω·cm

IEC 60093

Technological properties

Property
Application areas

Main applications:

  • reathable membranes
  • Permanent antistactic additive
  • Note: this grade is not recommended by Arkema for usage in medical applications. For such applications Pebax® SA 01 MED should be used

    or

    Permanent Antistatic Solutions,Footwear - Midsoles / Foam,Permanent Antistatic Solutions E&E.

    Note: this grade is not recommended by Arkema for usage in medical applications. For such applications Pebax® SA 01 MED should be used

  • Certifications

    Food Contact

    Other

    Packaging:

  • This grade is delivered dried in sealed packaging (25 kg bags and 550 kg rigid containers) ready to be processed.

    Shelf life:

  • Two years from the delivery. For any use above this limit, please refer to our technical services.

  • Processing methods

    Injection Molding:

  • Typical melt temperature (Min / Recommended / Max): 200°C / 240°C / 270°C.
  • Typical mold temperature: 25–60°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.


    Extrusion:

  • Typical melt temperature (Min / Recommended / Max): 210°C / 220°C / 230°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.