Pebax® MV 1074 SA 01 MED

Alternative and trade names
TPA
Want to keep this datasheet? Save it now in your required format

Description

Polyether block amide Pebax® MV 1074 SA 01 MED resin is a thermoplastic elastomer made of flexible and hydrophilic polyether and rigid polyamide. Hydrophilic Pebax® MV 1074 SA 01 MED resin is suitable for extrusion or coextrusion and offers excellent high moisture absorption properties in wet environments, enhancing lubricity against bodily tissue.

Pebax® MV 1074 SA 01 MED resin is also an inherently dissipative polymer and can be dry blended or compounded with a polymer matrix to lower the surface resistivity of the final part. This grade offers the highest quality and it is specially designed to meet the stringent requirements of the medical applications such as minimally invasive devices. Upon request, letters regarding USP Class VI compliance can be provided. Refractive index according to an internal method is 1.502.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting Standard

Density

1.07 g/cm³

Show Supplier Material materials with Density of 1.07 g/cm³

dry

ISO 1183

Limiting oxygen index

19 %

Show Supplier Material materials with Limiting oxygen index of 19 %

dry

ISO 4589-1/-2

Moisture absorption

1.4 %

Show Supplier Material materials with Moisture absorption of 1.4 %

Sim. to ISO 62

Mechanical

PropertyValueConditionTesting StandardComment

Elastic modulus

0.08 GPa

Show Supplier Material materials with Elastic modulus of 0.08 GPa

cond.

ISO 527-1/-2

0.097 GPa

Show Supplier Material materials with Elastic modulus of 0.097 GPa

dry

ISO 527-1/-2

Elongation

50 %

Show Supplier Material materials with Elongation of 50 %

cond., dry

ISO 527-1/-2

min.

500 %

Show Supplier Material materials with Elongation of 500 %

dry

ISO 527-3

700 %

Show Supplier Material materials with Elongation of 700 %

dry

ISO 527-3

Transverse

Hardness, Shore D

40 [-]

Show Supplier Material materials with Hardness, Shore D of 40 [-]

dry

ISO 7619-1

15 seconds

Impact strength, Charpy notched

No Break at 23 and -30°C

cond., dry

ISO 179/1eA

Impact strength, Charpy unnotched

No Break at 23 and -30°C

dry and cond.

ISO 179/1eU

Tensile strength

32 MPa

Show Supplier Material materials with Tensile strength of 32 MPa

dry

ISO 527-3

34 MPa

Show Supplier Material materials with Tensile strength of 34 MPa

dry

ISO 527-3

Transverse

Thermal

PropertyValueConditionTesting StandardComment

Glass transition temperature

-40 °C

Show Supplier Material materials with Glass transition temperature of -40 °C

dry

ISO 11357-1/-2

10°C/min

Melting point

158 °C

Show Supplier Material materials with Melting point of 158 °C

dry

ISO 11357-1/-3

10°C/min

Electrical

PropertyValueConditionTesting Standard

Dielectric strength

5 kV/mm

Show Supplier Material materials with Dielectric strength of 5 kV/mm

dry

IEC 60243-1

Surface resistivity

3e+09 Ω/sq

Show Supplier Material materials with Surface resistivity of 3e+09 Ω/sq

cond.

IEC 60093

Volume resistivity

2.5e+07 Ω·cm

Show Supplier Material materials with Volume resistivity of 2.5e+07 Ω·cm

cond.

IEC 60093

1.5e+11 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.5e+11 Ω·cm

dry

IEC 60093

Technological properties

Property
Application areas

Permanent Antistatic Solutions,Antistatic/Breathable,Healthcare-Other,IV Bags,Medical Catheters

Certifications

USP Class VI

Processing methods

Injection Molding:

  • Typical melt temperature (Min / Recommended / Max): 200°C / 240°C / 270°C.
  • Typical mold temperature: 25–60°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.


    Extrusion:

  • Typical melt temperature (Min / Recommended / Max): 210°C / 220°C / 230°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.