Pebax® MV 1074 SP 01

Alternative and trade names
TPA

Want to keep this datasheet? Save it now in your required format

Description

Polyether block amide Pebax® MV 1074 SP 01 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide.

Pebax® MV 1074 SP 01 resin is an inherently dissipative polymer and can be dry blended or compounded with an isolative polymer to lower the surface resistivity. This hydrophilic grade when extruded into either a thin film or laminated on to a substrate offers excellent permeability to moisture vapor while remaining waterproof. This SP grade has been developed to be heat and UV resistant. Refractive index according to an internal method is 1.502.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Condition	Testing Standard
Density	1.07 g/cm³ Show Supplier Material materials with Density of 1.07 g/cm³	dry	ISO 1183
Limiting oxygen index	19 % Show Supplier Material materials with Limiting oxygen index of 19 %	dry	ISO 4589-1/-2
Moisture absorption	1.4 % Show Supplier Material materials with Moisture absorption of 1.4 %		Sim. to ISO 62
Water absorption	48 % Show Supplier Material materials with Water absorption of 48 %		Sim. to ISO 62

Mechanical

Property	Value	Condition	Testing Standard	Comment
Elastic modulus	0.08 GPa Show Supplier Material materials with Elastic modulus of 0.08 GPa	cond.	ISO 527-1/-2
	0.097 GPa Show Supplier Material materials with Elastic modulus of 0.097 GPa	dry	ISO 527-1/-2
Elongation	50 % Show Supplier Material materials with Elongation of 50 %	cond., dry	ISO 527-1/-2	min.
	500 % Show Supplier Material materials with Elongation of 500 %	dry	ISO 527-3
	700 % Show Supplier Material materials with Elongation of 700 %	dry	ISO 527-3	Transverse
Hardness, Shore D	40 [-] Show Supplier Material materials with Hardness, Shore D of 40 [-]	dry	ISO 7619-1	15 seconds
Impact strength, Charpy notched	No Break at 23°C	cond.	ISO 179/1eA
	No Break at 23 and -30°C	dry	ISO 179/1eA
Impact strength, Charpy unnotched	No Break at 23 and -30°C	dry and cond.	ISO 179/1eU
Tensile strength	32 MPa Show Supplier Material materials with Tensile strength of 32 MPa	dry	ISO 527-3
	34 MPa Show Supplier Material materials with Tensile strength of 34 MPa	dry	ISO 527-3	Transverse

Thermal

Property	Value	Condition	Testing Standard	Comment
Glass transition temperature	-40 °C Show Supplier Material materials with Glass transition temperature of -40 °C	dry	ISO 11357-1/-2	10°C/min
Melting point	158 °C Show Supplier Material materials with Melting point of 158 °C	dry	ISO 11357-1/-3	10°C/min

Electrical

Property	Value	Condition	Testing Standard
Dielectric strength	5 kV/mm Show Supplier Material materials with Dielectric strength of 5 kV/mm	dry	IEC 60243-1
Surface resistivity	3e+09 Ω/sq Show Supplier Material materials with Surface resistivity of 3e+09 Ω/sq	cond.	IEC 60093
Volume resistivity	2.5e+07 Ω·cm Show Supplier Material materials with Volume resistivity of 2.5e+07 Ω·cm	cond.	IEC 60093
	1.5e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1.5e+11 Ω·cm	dry	IEC 60093

Technological properties

Property

Application areas

Permanent Antistatic Solutions,Footwear - Midsoles / Foam,Permanent Antistatic Solutions E&E

Processing methods

Injection Molding:

Typical melt temperature (Min / Recommended / Max): 200°C / 240°C / 270°C.

Typical mold temperature: 25–60°C.

Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.

Extrusion:

Typical melt temperature (Min / Recommended / Max): 210°C / 220°C / 230°C.

Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.