Pebax® MV 3000 SP 01

Alternative and trade names
TPA
Want to keep this datasheet? Save it now in your required format

Description

Polyether block Pebax® MV 3000 SP 01 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This hydrophilic grade when extruded into either a thin film or laminated on to a substrate offers excellent permeability to moisture vapor while remaining waterproof. This SP grade is specifically designed for outdoor application that needs excellent weather resistance properties.

This material data has been provided by Arkema Technical Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting Standard

Density

1.02 g/cm³

Show Supplier Material materials with Density of 1.02 g/cm³

dry

ISO 1183

Moisture absorption

1 %

Show Supplier Material materials with Moisture absorption of 1 %

Sim. to ISO 62

Water absorption

28 %

Show Supplier Material materials with Water absorption of 28 %

Sim. to ISO 62

Mechanical

PropertyValueConditionTesting StandardComment

Elastic modulus

0.045 GPa

Show Supplier Material materials with Elastic modulus of 0.045 GPa

cond.

ISO 527-1/-2

Elongation

50 %

Show Supplier Material materials with Elongation of 50 %

cond.

ISO 527-1/-2

min.

Hardness, Shore D

35 [-]

Show Supplier Material materials with Hardness, Shore D of 35 [-]

dry

ISO 7619-1

15 seconds

Thermal

PropertyValueConditionTesting StandardComment

Melting point

158 °C

Show Supplier Material materials with Melting point of 158 °C

dry

ISO 11357-1/-3

10°C/min

Technological properties

Property
Application areas

Breathable Films - Housewrap,Hot Melt Adhesives - Sports Apparel and Underwear

Processing methods

Extrusion:

  • Cast Film, Typical melt temperature : 240 - 250°C.
  • Blown Film, Typical melt temperature : 190 - 210°C.
  • Coating, Typical melt temperature : 240 - 250°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 70-80°C.