Pebax® Rnew® 30R51 SA 01

Alternative and trade names
TPA

Want to keep this datasheet? Save it now in your required format

Description

Polyether block Pebax® Rnew® 30R51 SA 01 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide based on renewable resources.

Pebax® Rnew® 30R51 SA 01 resin is an inherently antistatic polymer and can be dry blended or compounded with a polymer matrix to lower the surface resistivity of the final part. This grade is particularly recommended for PMMA matrices. This hydrophilic grade when extruded into either a thin film or laminated on to a substrate offers excellent permeability to moisture vapor while remaining waterproof. The percentage of renewable carbon according to ASTM D6866 is 41%

. Refractive index according to an internal method is 1.49.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Condition	Testing Standard
Bio-based content	41 % Show Supplier Material materials with Bio-based content of 41 %
Density	1.01 g/cm³ Show Supplier Material materials with Density of 1.01 g/cm³	dry	ISO 1183
Moisture absorption	2.5 % Show Supplier Material materials with Moisture absorption of 2.5 %		Sim. to ISO 62
Water absorption	20 % Show Supplier Material materials with Water absorption of 20 %		Sim. to ISO 62

Mechanical

Property	Value	Condition	Testing Standard	Comment
Elastic modulus	0.059 GPa Show Supplier Material materials with Elastic modulus of 0.059 GPa	cond.	ISO 527-1/-2
Elongation	50 % Show Supplier Material materials with Elongation of 50 %	cond.	ISO 527-1/-2	min.
Hardness, Shore D	30 [-] Show Supplier Material materials with Hardness, Shore D of 30 [-]	dry	ISO 7619-1	15 seconds

Thermal

Property	Value	Condition	Testing Standard	Comment
Melting point	150 °C Show Supplier Material materials with Melting point of 150 °C	dry	ISO 11357-1/-3	10°C/min

Electrical

Property	Value	Condition	Testing Standard
Surface resistivity	1e+08 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+08 Ω/sq	cond.	IEC 60093
Volume resistivity	1e+08 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+08 Ω·cm	cond.	IEC 60093
	1e+10 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+10 Ω·cm	dry	IEC 60093

Technological properties

Property

Application areas

Breathable Films - Housewrap,Permanent Antistatic Solutions,Eyewear Frames,Permanent Antistatic Solutions E&E

Processing methods

Injection Molding:

Typical melt temperature (Min / Recommended / Max): 200°C / 240°C / 270°C.

Typical mold temperature: 25–60°C.

Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.

Extrusion:

Typical melt temperature (Min / Recommended / Max): 210°C / 220°C / 230°C.

Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.