Pebax® Rnew® 63R53 SP 01

Alternative and trade names
TPA
Want to keep this datasheet? Save it now in your required format

Description

Polyether blockPebax® Rnew® 63R53 SP 01 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide based on renewable resources. This SP grade has been developed to be heat and UV resistant. The percentage of renewable carbon according to ASTM D6866 is 77-81%.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting Standard

Bio-based content

77 %

Show Supplier Material materials with Bio-based content of 77 %

81 %

Show Supplier Material materials with Bio-based content of 81 %

Density

1.03 g/cm³

Show Supplier Material materials with Density of 1.03 g/cm³

dry

ISO 1183

Moisture absorption

0.8 %

Show Supplier Material materials with Moisture absorption of 0.8 %

Sim. to ISO 62

Water absorption

1.5 %

Show Supplier Material materials with Water absorption of 1.5 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

0.245 GPa

Show Supplier Material materials with Elastic modulus of 0.245 GPa

cond.

ISO 527-1/-2

Elongation

50 %

Show Supplier Material materials with Elongation of 50 %

cond.

ISO 527-1/-2

min. | nominal

Elongation at yield

40 %

Show Supplier Material materials with Elongation at yield of 40 %

cond.

ISO 527-1/-2

Hardness, Shore D

56 [-]

Show Supplier Material materials with Hardness, Shore D of 56 [-]

dry

ISO 7619-1

15 seconds

Impact strength, Charpy notched

-30 °C

22 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 22 kJ/m²

cond.

ISO 179/1eA

No Break at 23°C

Impact strength, Charpy unnotched

No Break at 23 and -30°C

cond.

ISO 179/1eU

Yield strength

24 MPa

Show Supplier Material materials with Yield strength of 24 MPa

cond.

ISO 527-1/-2

Thermal

PropertyValueConditionTesting StandardComment

Melting point

180 °C

Show Supplier Material materials with Melting point of 180 °C

dry

ISO 11357-1/-3

10°C/min

Vicat softening temperature

168 °C

Show Supplier Material materials with Vicat softening temperature of 168 °C

ISO 306

50°C/h 50N

Rheological Properties

PropertyValueConditionTesting StandardComment

Shrinkage

1.2 %

Show Supplier Material materials with Shrinkage of 1.2 %

dry

ISO 294-4

Transverse

1.3 %

Show Supplier Material materials with Shrinkage of 1.3 %

dry

ISO 294-4

Technological properties

Property
Application areas

Tubing and Hoses,Eyewear Frames,Footwear - Outsoles,Ski Boots

Processing methods

Injection Molding:

  • Typical melt temperature (Min / Recommended / Max) : 230°C / 260°C / 290°C
  • Typical mold temperature : 25 – 60°C
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-8 hours at 65-75°C


    Extrusion:

  • Typical melt temperature (Min / Recommended / Max): 210°C / 225°C / 240°C
  • Drying time and temperature (only necessary for bags opened for more than two hours): 4-8 hours at 65-75°C