Rilsamid® AESNO P302 TL

Alternative and trade names
PA12-I
Want to keep this datasheet? Save it now in your required format

Description

PA12-HIP, EHL, 22-004

Rilsamid® AESNO P302 TL resin is a natural polyamide. This grade is plasticized and designed for tube extrusion.

Rilsamid® AESNO P302 TL resin falls into the PA12-HIPHL category according to DIN 73378.

This material data has been provided by Arkema High Performance Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.03 g/cm³

Show Supplier Material materials with Density of 1.03 g/cm³

ISO 1183

Water absorption

23.0 °C

1.2 %

Show Supplier Material materials with Water absorption of 1.2 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

0.48 GPa

Show Supplier Material materials with Elastic modulus of 0.48 GPa

ISO 527-1/-2

Elongation

23.0 °C

50 %

Show Supplier Material materials with Elongation of 50 %

min., ISO 527-1/-2, nominal

Elongation at yield

23.0 °C

24 %

Show Supplier Material materials with Elongation at yield of 24 %

ISO 527-1/-2

Impact strength, Charpy notched

-30.0 °C

4 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 4 kJ/m²

ISO 179/1eA

23.0 °C

46 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 46 kJ/m²

ISO 179/1eA

Yield strength

23.0 °C

28 MPa

Show Supplier Material materials with Yield strength of 28 MPa

ISO 527-1/-2

Impact strength, Charpy unnotched

No break @ 23,-30°C, ISO 179/1eU

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.5E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.5E-4 1/K

ISO 11359-1/-2

Melting point

174 °C

Show Supplier Material materials with Melting point of 174 °C

ISO 11357-1/-3, 10°C/min

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Supplier Material materials with Comparative tracking index of 600 V

IEC 60112, Conditioned

Dielectric strength

23.0 °C

41 kV/mm

Show Supplier Material materials with Dielectric strength of 41 kV/mm

IEC 60243-1

Volume resistivity

23.0 °C

1.00E+14 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+14 Ω·cm

IEC 60093

Rheological Properties

PropertyValueComment

Melt volume-flow rate

13 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 13 cm³/10min

ISO 1133, 235°C/5kg

Technological properties

Property
Application areas

Air Brake Tubing,Auto - Water Cooling Circuit,Fuel Management - Fuel Lines,Pneumatic Tubing,Tubing and Hoses,Sports Equipment

Processing methods

Injection Molding:

  • Melt temperature (°C) ISO 294: 270
  • Mold temperature (°C) ISO 10724: 50
  • Injection velocity (mm/s) ISO 294: -
  • Pressure at hold (MPa) ISO 294: 16