Rilsamid® AESNO P40 TL

Alternative and trade names
PA12
Want to keep this datasheet? Save it now in your required format

Description

PA12-P, EHL, 22-004

Rilsamid® AESNO P40 TL resin is a natural polyamide. This grade is plasticized and designed for tube extrusion.

Rilsamid® AESNO P40 TL resin falls into the PA12-PHL category according to DIN 73378.

This material data has been provided by Arkema Technical Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting Standard

Density

1.03 g/cm³

Show Supplier Material materials with Density of 1.03 g/cm³

dry

ISO 1183

Water absorption

1.2 %

Show Supplier Material materials with Water absorption of 1.2 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

0.38 GPa

Show Supplier Material materials with Elastic modulus of 0.38 GPa

cond.

ISO 527-1/-2

0.43 GPa

Show Supplier Material materials with Elastic modulus of 0.43 GPa

dry

ISO 527-1/-2

Elongation

50 %

Show Supplier Material materials with Elongation of 50 %

cond., dry

ISO 527-1/-2

min. | nominal

Elongation at yield

24 %

Show Supplier Material materials with Elongation at yield of 24 %

dry

ISO 527-1/-2

26 %

Show Supplier Material materials with Elongation at yield of 26 %

cond.

ISO 527-1/-2

Impact strength, Charpy notched

-30 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 5 kJ/m²

cond.

ISO 179/1eA

No Break at 23°C

Impact strength, Charpy unnotched

No Break at 23 and -30°C

cond.

ISO 179/1eU

Puncture energy

-30 °C

60 J

Show Supplier Material materials with Puncture energy of 60 J

cond.

ISO 6603-2

Puncture force

-30 °C

5600 N

Show Supplier Material materials with Puncture force of 5600 N

cond.

ISO 6603-2

Thermal

PropertyValueConditionTesting StandardComment

Coefficient of thermal expansion

0.00014 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 0.00014 1/K

dry

ISO 11359-1/-2

Melting point

174 °C

Show Supplier Material materials with Melting point of 174 °C

dry

ISO 11357-1/-3

10°C/min

Vicat softening temperature

130 °C

Show Supplier Material materials with Vicat softening temperature of 130 °C

ISO 306

50°C/h 50N

Electrical

PropertyValueConditionTesting Standard

Comparative tracking index

600 V

Show Supplier Material materials with Comparative tracking index of 600 V

cond.

IEC 60112

Dielectric strength

24 kV/mm

Show Supplier Material materials with Dielectric strength of 24 kV/mm

cond.

IEC 60243-1

Surface resistivity

5e+11 Ω/sq

Show Supplier Material materials with Surface resistivity of 5e+11 Ω/sq

cond.

IEC 60093

Volume resistivity

1e+09 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+09 Ω·cm

cond.

IEC 60093

Rheological Properties

PropertyValueConditionTesting StandardComment

Melt volume-flow rate

16 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 16 cm³/10min

dry

ISO 1133

235°C/5kg

Technological properties

Property
Application areas

Air Brake Tubing,Fuel Management - Fuel Lines,Pneumatic Tubing,Tubing and Hoses,Sports Equipment,Antitermite Cables,Performance Wire,Underground Fuel Containment

Processing methods

Injection Molding:

  • Melt temperature (°C) ISO 294: 270
  • Mold temperature (°C) ISO 10724: 50
  • Injection velocity (mm/s) ISO 294: -
  • Pressure at hold (MPa) ISO 294: 16