Rilsamid® ASR 13

Alternative and trade names
PA12-CF15
Want to keep this datasheet? Save it now in your required format

Description

PA12, MHL, 18-080, CF 15

Rilsamid® ASR 13 resin is a carbon fiber reinforced polyamide. This black colored grade is designed for injection moulding.

This material data has been provided by Arkema High Performance Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.08 g/cm³

Show Supplier Material materials with Density of 1.08 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.6 %

Show Supplier Material materials with Moisture absorption of 0.6 %

Sim. to ISO 62

Water absorption

23.0 °C

1.5 %

Show Supplier Material materials with Water absorption of 1.5 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

9.6 GPa

Show Supplier Material materials with Elastic modulus of 9.6 GPa

ISO 527-1/-2

Elongation

23.0 °C

4 %

Show Supplier Material materials with Elongation of 4 %

ISO 527-1/-2, nominal, Conditioned

Impact strength, Charpy notched

-30.0 °C

8 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 8 kJ/m²

ISO 179/1eA

23.0 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

-30.0 °C

47 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 47 kJ/m²

ISO 179/1eU

23.0 °C

45 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 45 kJ/m²

ISO 179/1eU

Unlock all property charts

Tensile strength

23.0 °C

127 MPa

Show Supplier Material materials with Tensile strength of 127 MPa

ISO 527-1/-2

Thermal

PropertyValueComment

Melting point

178 °C

Show Supplier Material materials with Melting point of 178 °C

ISO 11357-1/-3, 10°C/min

Thermal decomposition in air

223 °C

Show Supplier Material materials with Thermal decomposition in air of 223 °C

TGA, 1% wt. loss

Thermal decomposition in nitrogen

223 °C

Show Supplier Material materials with Thermal decomposition in nitrogen of 223 °C

TGA, 1% wt. loss

Rheological Properties

PropertyValueComment

Melt volume-flow rate

10 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 10 cm³/10min

ISO 1133, 235°C/5kg

Technological properties

Property
Application areas

Connectors

Fillers

15% Carbon Fiber

Processing methods

Injection Molding:

  • Melt temperature (°C) ISO 294: 280
  • Mold temperature (°C) ISO 10724: 60
  • Injection velocity (mm/s) ISO 294: -
  • Pressure at hold (MPa) ISO 294: 19