Rilsan® 8020

Alternative and trade names
PA*
Want to keep this datasheet? Save it now in your required format

Description

Rilsan® 8020 resin is a translucent flexible copolyamide based on renewable resources and without plasticizer. This grade is specially designed for medical uses.

This material data has been provided by Arkema High Performance Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.02 g/cm³

Show Supplier Material materials with Density of 1.02 g/cm³

ISO 1183

Water absorption

23.0 °C

0.8 %

Show Supplier Material materials with Water absorption of 0.8 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

50 %

Show Supplier Material materials with Elongation of 50 %

min., ISO 527-1/-2, nominal, Conditioned

Elongation at yield

23.0 °C

21 %

Show Supplier Material materials with Elongation at yield of 21 %

ISO 527-1/-2, Conditioned

Yield strength

23.0 °C

24 MPa

Show Supplier Material materials with Yield strength of 24 MPa

ISO 527-1/-2, Conditioned

Thermal

PropertyValueComment

Melting point

172 °C

Show Supplier Material materials with Melting point of 172 °C

ISO 11357-1/-3, 10°C/min

Technological properties

Property
Application areas

Main applications:

  • Catheter
  • alloon catheter
  • Healthcare-Other,IV Bags,Medical Catheters

  • Other

    Packaging:

  • This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

    Shelf Life:

  • Two years from the delivery. For any use above this limit, please refer to our technical services.

  • Processing methods

    Extrusion:

  • Typical melt temperature (Min / Recommended / Max) : 220°C / 235°C / 250°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80°C.