Rilsan® BECV BLUE T8L

Alternative and trade names
PA11
Want to keep this datasheet? Save it now in your required format

Description

PA11, KHL, 18-010

Rilsan® BECV BLUE T8L resin is a polyamide 11 produced from a renewable source. This blue coloured grade is designed for cable coating but is also suitable for extrusion. The percentage of renewable carbon according to ASTM D6866 (calculated) is 95%.

This material data has been provided by Arkema Technical Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyValueConditionTesting Standard

Bio-based content

95 %

Show Supplier Material materials with Bio-based content of 95 %

Density

1.03 g/cm³

Show Supplier Material materials with Density of 1.03 g/cm³

dry

ISO 1183

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elongation

50 %

Show Supplier Material materials with Elongation of 50 %

cond.

ISO 527-1/-2

min. | nominal

Elongation at yield

7 %

Show Supplier Material materials with Elongation at yield of 7 %

cond.

ISO 527-1/-2

Hardness, Shore D

71 [-]

Show Supplier Material materials with Hardness, Shore D of 71 [-]

dry

ISO 7619-1

15 seconds

Impact strength, Charpy notched

-30 °C

12 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m²

cond.

ISO 179/1eA

23 °C

10 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m²

cond.

ISO 179/1eA

Impact strength, Charpy unnotched

No Break at 23 and -30°C

cond.

ISO 179/1eU

Yield strength

27 MPa

Show Supplier Material materials with Yield strength of 27 MPa

cond.

ISO 527-1/-2

Thermal

PropertyValueConditionTesting StandardComment

Melting point

189 °C

Show Supplier Material materials with Melting point of 189 °C

dry

ISO 11357-1/-3

10°C/min

Technological properties

Property
Application areas

Antitermite Cables

Processing methods

Injection Molding:

  • Typical melt temperature (Min / Recommended / Max) : 250°C / 260°C / 270°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80-90°C.