Rilsan® BES BLACK PR

Alternative and trade names
PA11
Want to keep this datasheet? Save it now in your required format

Description

PA11-P, EHL, 22-005

Rilsan® BES BLACK PR resin is a polyamide 11 produced from a renewable source. This black grade is plasticized and designed for extrusion.

This material data has been provided by Arkema High Performance Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.05 g/cm³

Show Supplier Material materials with Density of 1.05 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

50 %

Show Supplier Material materials with Elongation of 50 %

min., ISO 527-1/-2, nominal, Conditioned

Elongation at yield

23.0 °C

32 %

Show Supplier Material materials with Elongation at yield of 32 %

ISO 527-1/-2, Conditioned

Hardness, Shore D

23.0 °C

63 [-]

Show Supplier Material materials with Hardness, Shore D of 63 [-]

ISO 7619-1, 15 seconds

Yield strength

23.0 °C

27 MPa

Show Supplier Material materials with Yield strength of 27 MPa

ISO 527-1/-2, Conditioned

Thermal

PropertyValueComment

Melting point

182 °C

Show Supplier Material materials with Melting point of 182 °C

ISO 11357-1/-3, 10°C/min

Technological properties

Property
Application areas

Main applications:

  • Fluid transportation
  • Tubing for use in motor vehicle
  • Pneumatic Tubing,Sports Equipment,Performance Wire,Wire and Cables

  • Other

    Packaging:

  • This grade is delivered dried in sealed packaging (25 kg bags,44 lb bags, 1000 lb rigid containers) ready to be processed.

    Shelf Life:

  • Two years from the delivery. For any use above this limit, please refer to our technical services.

  • Processing methods

    Extrusion:

  • Typical melt temperature (Min / Recommended / Max) : 230°C / 250°C / 280°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80-90°C.