Rilsan® BESN BLACK P123 TL

Alternative and trade names
PA11
Want to keep this datasheet? Save it now in your required format

Description

PA11, EHLN, 22-010

Rilsan® BESN BLACK P123 TL resin is a flexible polyamide 11 produced from a renewable source. This black grade is designed for extrusion typically for cooling application and for Adblue circuits (SCR). The percentage of renewable carbon according to ASTM D6866 (calculated) is 98%.

This material data has been provided by Arkema Technical Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyValueConditionTesting Standard

Bio-based content

98 %

Show Supplier Material materials with Bio-based content of 98 %

Density

1 g/cm³

Show Supplier Material materials with Density of 1 g/cm³

dry

ISO 1183

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elongation

50 %

Show Supplier Material materials with Elongation of 50 %

cond.

ISO 527-1/-2

min. | nominal

Elongation at yield

33 %

Show Supplier Material materials with Elongation at yield of 33 %

cond.

ISO 527-1/-2

Impact strength, Charpy notched

-30 °C

25 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 25 kJ/m²

cond.

ISO 179/1eA

23 °C

100 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 100 kJ/m²

cond.

ISO 179/1eA

Thermal

PropertyValueConditionTesting StandardComment

Melting point

189 °C

Show Supplier Material materials with Melting point of 189 °C

dry

ISO 11357-1/-3

10°C/min

Technological properties

Property
Application areas

Auto - Water Cooling Circuit,Emission Control Systems - SCR Lines and Tanks

Processing methods

Injection Molding:

  • Typical melt temperature (Min / Recommended / Max) : 260°C / 275°C / 290°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-8 hours at 80-90°C.