Rilsan® BESN BLACK P20 TL

Alternative and trade names
PA11

Want to keep this datasheet? Save it now in your required format

Description

PA11-P,E HL, 22-005

Rilsan® BESN BLACK P20 TL resin is a polyamide 11 produced from a renewable source. This black grade is plasticized and designed for extrusion. The percentage of renewable carbon according to ASTM D6866 (calculated) is 92%.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Condition	Testing Standard
Bio-based content	92 % Show Supplier Material materials with Bio-based content of 92 %
Density	1.04 g/cm³ Show Supplier Material materials with Density of 1.04 g/cm³	dry	ISO 1183
Water absorption	1.8 % Show Supplier Material materials with Water absorption of 1.8 %		Sim. to ISO 62

Mechanical

Property	Temperature	Value	Condition	Testing Standard	Comment
Elastic modulus		0.56 GPa Show Supplier Material materials with Elastic modulus of 0.56 GPa	cond.	ISO 527-1/-2
Elongation		50 % Show Supplier Material materials with Elongation of 50 %	cond.	ISO 527-1/-2	min. \| nominal
Elongation at yield		33 % Show Supplier Material materials with Elongation at yield of 33 %	cond.	ISO 527-1/-2
Impact strength, Charpy notched	-30 °C	10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m²	cond.	ISO 179/1eA
	23 °C	70 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 70 kJ/m²	cond.	ISO 179/1eA
Impact strength, Charpy unnotched		No Break at 23 and -30°C	cond.	ISO 179/1eU
Yield strength		32 MPa Show Supplier Material materials with Yield strength of 32 MPa	cond.	ISO 527-1/-2

Thermal

Property	Value	Condition	Testing Standard	Comment
Melting point	182 °C Show Supplier Material materials with Melting point of 182 °C	dry	ISO 11357-1/-3	10°C/min

Technological properties

Property

Application areas

Fluid Management - Brakebooster Lines,Fuel Management - Fuel Lines,Fuel Management - In-Tank and Fuel Venting Lines,Pneumatic Tubing

Processing methods

Injection Molding:

Melt temperature (°C) ISO 294: 270

Mold temperature (°C) ISO 10724: 50

Injection velocity (mm/s) ISO 294: -

Pressure at hold (MPa) ISO 294: 16

Extrusion:

Typical melt temperature (Min / Recommended / Max) : 230°C / 250°C / 280°C.

Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80-90°C.

Rilsan® BESN BLACK P20 TL

Description

Ashby charts

Applications

Materials by this supplier

Properties