Rilsan® BESNO P20 TL

Alternative and trade names
PA11
Want to keep this datasheet? Save it now in your required format

Description

PA11-P, EHL, 22-005

Rilsan® BESNO P20 TL resin is a polyamide 11 produced from a renewable source. This natural grade is plasticized and designed for extrusion. The percentage of renewable carbon according to ASTM D6866 (calculated) is 93%.

This material data has been provided by Arkema Technical Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting Standard

Bio-based content

93 %

Show Supplier Material materials with Bio-based content of 93 %

Density

1.04 g/cm³

Show Supplier Material materials with Density of 1.04 g/cm³

dry

ISO 1183

Water absorption

1.8 %

Show Supplier Material materials with Water absorption of 1.8 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

0.51 GPa

Show Supplier Material materials with Elastic modulus of 0.51 GPa

cond.

ISO 527-1/-2

Elongation

50 %

Show Supplier Material materials with Elongation of 50 %

cond.

ISO 527-1/-2

min. | nominal

Elongation at yield

40 %

Show Supplier Material materials with Elongation at yield of 40 %

cond.

ISO 527-1/-2

Hardness, Shore D

64 [-]

Show Supplier Material materials with Hardness, Shore D of 64 [-]

dry

ISO 7619-1

15 seconds

Impact strength, Charpy notched

-30 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²

cond.

ISO 179/1eA

No Break at 23°C

Impact strength, Charpy unnotched

No Break at 23 and -30°C

cond.

ISO 179/1eU

Yield strength

29 MPa

Show Supplier Material materials with Yield strength of 29 MPa

cond.

ISO 527-1/-2

Thermal

PropertyValueConditionTesting StandardComment

Coefficient of thermal expansion

0.0001 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 0.0001 1/K

dry

ISO 11359-1/-2

Melting point

182 °C

Show Supplier Material materials with Melting point of 182 °C

dry

ISO 11357-1/-3

10°C/min

Vicat softening temperature

146 °C

Show Supplier Material materials with Vicat softening temperature of 146 °C

ISO 306

50°C/h 50N

Electrical

PropertyValueConditionTesting Standard

Dielectric strength

24 kV/mm

Show Supplier Material materials with Dielectric strength of 24 kV/mm

cond.

IEC 60243-1

Surface resistivity

2e+12 Ω/sq

Show Supplier Material materials with Surface resistivity of 2e+12 Ω/sq

cond.

IEC 60093

Volume resistivity

1e+10 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+10 Ω·cm

cond.

IEC 60093

Rheological Properties

PropertyValueConditionTesting StandardComment

Melt volume-flow rate

2 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 2 cm³/10min

dry

ISO 1133

235°C/5kg

Technological properties

Property
Application areas

Fluid Management - Brakebooster Lines,Fuel Management - Fuel Lines,Fuel Management - In-Tank and Fuel Venting Lines,Pneumatic Tubing,Offshore Oil Production - Anti Wear Tapes

Processing methods

Injection Molding:

  • Melt temperature (°C) ISO 294: 270
  • Mold temperature (°C) ISO 10724: 50
  • Injection velocity (mm/s) ISO 294: -
  • Pressure at hold (MPa) ISO 294: 16

  • Extrusion:

  • Typical melt temperature (Min / Recommended / Max) : 230°C / 250°C / 280°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-8 hours at 80-90°C.