Rilsan® BESNO P210 TL

Alternative and trade names
PA11
Want to keep this datasheet? Save it now in your required format

Description

PA11-HIP, EHL, 22-005

Rilsan® BESNO P210 TL resin is a polyamide 11 produced from a renewable source. This natural grade is plasticized and designed for extrusion.

Rilsan® BESNO P210 TL resin falls into the PA11-PHLY category according to DIN 73378 and fulfils all specifications according to DIN 74324, ISO 7628, NFR 12632 and SAE J844 The percentage of renewable carbon according to ASTM D6866 (calculated) is 89%.

This material data has been provided by Arkema High Performance Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Bio-based content

89 %

Show Supplier Material materials with Bio-based content of 89 %

ASTM D6866

Density

23.0 °C

1.03 g/cm³

Show Supplier Material materials with Density of 1.03 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

0.59 GPa

Show Supplier Material materials with Elastic modulus of 0.59 GPa

ISO 527-1/-2, Conditioned

Elongation

23.0 °C

50 %

Show Supplier Material materials with Elongation of 50 %

min., ISO 527-1/-2, nominal, Conditioned

Elongation at yield

23.0 °C

35 %

Show Supplier Material materials with Elongation at yield of 35 %

ISO 527-1/-2, Conditioned

Hardness, Shore D

23.0 °C

67 [-]

Show Supplier Material materials with Hardness, Shore D of 67 [-]

ISO 7619-1, 15 seconds

Yield strength

23.0 °C

30 MPa

Show Supplier Material materials with Yield strength of 30 MPa

ISO 527-1/-2, Conditioned

Thermal

PropertyValueComment

Melting point

184 °C

Show Supplier Material materials with Melting point of 184 °C

ISO 11357-1/-3, 10°C/min

Technological properties

Property
Application areas

Main applications:

  • Fluid transportation
  • Tubing for use in motor vehicle

  • Other

    Packaging:

  • This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

    Shelf Life:

  • Two years from the delivery. For any use above this limit, please refer to our technical services.

  • Processing methods

    Extrusion:

  • Typical melt temperature (Min / Recommended / Max) : 230°C / 250°C / 280°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-8 hours at 80-90°C.