Rilsan® BESNO P40 TL

Alternative and trade names
PA11
Want to keep this datasheet? Save it now in your required format

Description

PA11-P, EHL, 22-003

Rilsan® BESNO P40 TL resin is a polyamide 11 produced from a renewable source. This natural grade is plasticized and designed for extrusion. The percentage of renewable carbon according to ASTM D6866 (calculated) is 89%.

This material data has been provided by Arkema High Performance Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Bio-based content

89 %

Show Supplier Material materials with Bio-based content of 89 %

ASTM D6866

Density

23.0 °C

1.04 g/cm³

Show Supplier Material materials with Density of 1.04 g/cm³

ISO 1183

Water absorption

23.0 °C

1.6 %

Show Supplier Material materials with Water absorption of 1.6 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

0.35 GPa

Show Supplier Material materials with Elastic modulus of 0.35 GPa

ISO 527-1/-2, Conditioned

Elongation

23.0 °C

50 %

Show Supplier Material materials with Elongation of 50 %

min., ISO 527-1/-2, nominal, Conditioned

Elongation at yield

23.0 °C

50 %

Show Supplier Material materials with Elongation at yield of 50 %

ISO 527-1/-2, Conditioned

Hardness, Shore D

23.0 °C

60 [-]

Show Supplier Material materials with Hardness, Shore D of 60 [-]

ISO 7619-1, 15 seconds

Puncture energy

-30.0 °C

70 J

Show Supplier Material materials with Puncture energy of 70 J

ISO 6603-2, Conditioned

Puncture force

-30.0 °C

6000 N

Show Supplier Material materials with Puncture force of 6000 N

ISO 6603-2, Conditioned

Yield strength

23.0 °C

26 MPa

Show Supplier Material materials with Yield strength of 26 MPa

ISO 527-1/-2, Conditioned

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.1E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.1E-4 1/K

ISO 11359-1/-2

Heat deflection temperature, 0.45 MPa

130 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 130 °C

ISO 75-1/-2

Heat deflection temperature, 1.80 MPa

45 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 45 °C

ISO 75-1/-2

Melting point

181 °C

Show Supplier Material materials with Melting point of 181 °C

ISO 11357-1/-3, 10°C/min

Vicat softening temperature

140 °C

Show Supplier Material materials with Vicat softening temperature of 140 °C

ISO 306, 50°C/h 50N

Electrical

PropertyTemperatureValueComment

Dielectric constant, 100Hz

23.0 °C

9 [-]

Show Supplier Material materials with Dielectric constant, 100Hz of 9 [-]

IEC 60250

Dielectric constant, 1MHz

23.0 °C

4 [-]

Show Supplier Material materials with Dielectric constant, 1MHz of 4 [-]

IEC 60250

Dielectric strength

23.0 °C

23 kV/mm

Show Supplier Material materials with Dielectric strength of 23 kV/mm

IEC 60243-1, Conditioned

Dissipation factor, 100Hz

23.0 °C

0.24 [-]

Show Supplier Material materials with Dissipation factor, 100Hz of 0.24 [-]

IEC 60250

Dissipation factor, 1MHz

23.0 °C

0.1 [-]

Show Supplier Material materials with Dissipation factor, 1MHz of 0.1 [-]

IEC 60250

Rheological Properties

PropertyValueComment

Melt volume-flow rate

3 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 3 cm³/10min

ISO 1133, 235°C/10kg

Technological properties

Property
Application areas

Main applications:

  • Tubing for use in motor vehicle
  • Air brake line
  • Air Brake Tubing,
  • Fluid Management - Brake booster Lines
  • Fuel Management - Fuel Lines, In-Tank and Fuel Venting Lines, Monofilaments, Pneumatic Tubing, Tubing and Hoses
  • Sports Equipment,
  • Performance Wire, Wire and Cables

  • Other

    Packaging:

  • This grade is delivered dried in sealed packaging (25 kg bags, 44 lb bags, 550 kg rigid containers, 1000 lb rigid containers) ready to be processed.

    Shelf Life:

  • Two years from the delivery. For any use above this limit, please refer to our technical services.

  • Processing methods

    Injection Molding:

  • Melt temperature (°C) ISO 294: 270
  • Mold temperature (°C) ISO 10724: 50
  • Injection velocity (mm/s) ISO 294: -
  • Pressure at hold (MPa) ISO 294: 16

  • Extrusion:

  • Typical melt temperature (Min / Recommended / Max) : 230°C / 250°C / 280°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-8 hours at 80-90°C.