Rilsan® BESNO TL

Alternative and trade names
PA11
Want to keep this datasheet? Save it now in your required format

Description

PA11,EHL,22-010

Rilsan® BESNO TL resin is a polyamide 11 produced from a renewable source. This natural grade is designed for extrusion. The percentage of renewable carbon according to ASTM D6866 (calculated) is 98%.

This material data has been provided by Arkema Technical Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting Standard

Bio-based content

98 %

Show Supplier Material materials with Bio-based content of 98 %

Density

1.02 g/cm³

Show Supplier Material materials with Density of 1.02 g/cm³

dry

ISO 1183

Water absorption

1.9 %

Show Supplier Material materials with Water absorption of 1.9 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

1.3 GPa

Show Supplier Material materials with Elastic modulus of 1.3 GPa

cond.

ISO 527-1/-2

Elongation

50 %

Show Supplier Material materials with Elongation of 50 %

cond.

ISO 527-1/-2

min. | nominal

Elongation at yield

5 %

Show Supplier Material materials with Elongation at yield of 5 %

cond.

ISO 527-1/-2

Hardness, Shore D

72 [-]

Show Supplier Material materials with Hardness, Shore D of 72 [-]

dry

ISO 7619-1

15 seconds

Impact strength, Charpy notched

-30 °C

12 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m²

cond.

ISO 179/1eA

23 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²

cond.

ISO 179/1eA

Impact strength, Charpy unnotched

No Break at 23 and -30°C

cond.

ISO 179/1eU

Puncture energy

-30 °C

70 J

Show Supplier Material materials with Puncture energy of 70 J

cond.

ISO 6603-2

Puncture force

-30 °C

6000 N

Show Supplier Material materials with Puncture force of 6000 N

cond.

ISO 6603-2

Yield strength

38 MPa

Show Supplier Material materials with Yield strength of 38 MPa

cond.

ISO 527-1/-2

Thermal

PropertyValueConditionTesting StandardComment

Coefficient of thermal expansion

8.5e-05 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 8.5e-05 1/K

dry

ISO 11359-1/-2

Melting point

186 °C

Show Supplier Material materials with Melting point of 186 °C

dry

ISO 11357-1/-3

10°C/min

Vicat softening temperature

160 °C

Show Supplier Material materials with Vicat softening temperature of 160 °C

ISO 306

50°C/h 50N

Flammability

At thickness 1.6 mm IEC 60695-11-10: HB and yellow card available

Electrical

PropertyValueConditionFrequencyTesting Standard

Dielectric constant

3 [-]

Show Supplier Material materials with Dielectric constant of 3 [-]

dry

100Hz

IEC 60250

3 [-]

Show Supplier Material materials with Dielectric constant of 3 [-]

dry

1MHz

IEC 60250

Dielectric strength

30 kV/mm

Show Supplier Material materials with Dielectric strength of 30 kV/mm

cond.

IEC 60243-1

Dissipation factor

0.0183 [-]

Show Supplier Material materials with Dissipation factor of 0.0183 [-]

dry

1MHz

IEC 60250

0.0308 [-]

Show Supplier Material materials with Dissipation factor of 0.0308 [-]

dry

100Hz

IEC 60250

Surface resistivity

1e+14 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+14 Ω/sq

cond.

IEC 60093

Volume resistivity

1e+12 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+12 Ω·cm

cond.

IEC 60093

Rheological Properties

PropertyValueConditionTesting StandardComment

Melt volume-flow rate

1 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 1 cm³/10min

dry

ISO 1133

235°C/2.16kg

Technological properties

Property
Application areas

Metal Tube Coating,Monofilaments,Pneumatic Tubing,Tubing and Hoses,Sports Equipment,Natural Gas Distribution- Fittings,Underground Fuel Containment

Certifications

Yellow Card

Processing methods

Injection Molding:

  • Melt temperature (°C) ISO 294: 260
  • Mold temperature (°C) ISO 10724: 50
  • Injection velocity (mm/s) ISO 294: -
  • Pressure at hold (MPa) ISO 294: 16

  • Extrusion:

  • Typical melt temperature (Min / Recommended / Max) : 230°C / 250°C / 280°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-8 hours at 80-90°C.