Rilsan® BMN G8 TLDA

Alternative and trade names
PA11-CD1
Want to keep this datasheet? Save it now in your required format

Description

PA11, MHLRS, 22-010 CD

Rilsan® BMN G8 TLDA resin is a polyamide 11 produced from a renewable source. This grade is designed for injection molding with improved friction properties and approuved for drinking water contact : WRAS (UK). The percentage of renewable carbon according to ASTM D6866 (calculated) is 94%.

This material data has been provided by Arkema High Performance Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Bio-based content

94 %

Show Supplier Material materials with Bio-based content of 94 %

ASTM D6866

Density

23.0 °C

1.03 g/cm³

Show Supplier Material materials with Density of 1.03 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

1.5 GPa

Show Supplier Material materials with Elastic modulus of 1.5 GPa

ISO 527-1/-2, Conditioned

Elongation

23.0 °C

50 %

Show Supplier Material materials with Elongation of 50 %

min., ISO 527-1/-2, nominal, Conditioned

Elongation at yield

23.0 °C

10 %

Show Supplier Material materials with Elongation at yield of 10 %

ISO 527-1/-2, Conditioned

Hardness, Shore D

23.0 °C

72 [-]

Show Supplier Material materials with Hardness, Shore D of 72 [-]

ISO 7619-1, 15 seconds

Yield strength

23.0 °C

40 MPa

Show Supplier Material materials with Yield strength of 40 MPa

ISO 527-1/-2, Conditioned

Thermal

PropertyValueComment

Melting point

186 °C

Show Supplier Material materials with Melting point of 186 °C

ISO 11357-1/-3, 10°C/min

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.4 %

Show Supplier Material materials with Shrinkage of 0.4 %

ISO 294-4 2577

Shrinkage, transverse

23.0 °C

0.8 %

Show Supplier Material materials with Shrinkage, transverse of 0.8 %

ISO 294-4 2577

Technological properties

Property
Application areas

Main applications:

  • Water meter parts

  • Fillers

    10% Carbon Black

    Other

    Packaging:

  • This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

    Shelf Life:

  • Two years from the delivery. For any use above this limit, please refer to our technical services.

  • Processing methods

    Injection Molding:

  • Typical melt temperature (Min / Recommended / Max) : 210°C / 230°C / 280°C.
  • Mold temperature : 20 - 60°C
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80-90°C.