Rilsan® BMNO P20 TLD

Alternative and trade names
PA11
Want to keep this datasheet? Save it now in your required format

Description

PA11-P, MHLR, 12-005

Rilsan® BMNO P20 TLD resin is a polyamide 11 produced from a renewable source. This natural grade is plasticized and designed for injection molding. The percentage of renewable carbon according to ASTM D6866 (calculated) is 92%.

This material data has been provided by Arkema High Performance Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Bio-based content

92 %

Show Supplier Material materials with Bio-based content of 92 %

ASTM D6866

Density

23.0 °C

1.05 g/cm³

Show Supplier Material materials with Density of 1.05 g/cm³

ISO 1183

Water absorption

23.0 °C

1.8 %

Show Supplier Material materials with Water absorption of 1.8 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

0.55 GPa

Show Supplier Material materials with Elastic modulus of 0.55 GPa

ISO 527-1/-2, Conditioned

Elongation

23.0 °C

50 %

Show Supplier Material materials with Elongation of 50 %

min., ISO 527-1/-2, nominal, Conditioned

Elongation at yield

23.0 °C

30 %

Show Supplier Material materials with Elongation at yield of 30 %

ISO 527-1/-2, Conditioned

Hardness, Shore D

23.0 °C

61 [-]

Show Supplier Material materials with Hardness, Shore D of 61 [-]

ISO 7619-1, 15 seconds

Yield strength

23.0 °C

32 MPa

Show Supplier Material materials with Yield strength of 32 MPa

ISO 527-1/-2, Conditioned

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1E-4 1/K

ISO 11359-1/-2

Heat deflection temperature, 0.45 MPa

135 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 135 °C

ISO 75-1/-2

Heat deflection temperature, 1.80 MPa

47 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 47 °C

ISO 75-1/-2

Melting point

186 °C

Show Supplier Material materials with Melting point of 186 °C

ISO 11357-1/-3, 10°C/min

Vicat softening temperature

145 °C

Show Supplier Material materials with Vicat softening temperature of 145 °C

ISO 306, 50°C/h 50N

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Supplier Material materials with Comparative tracking index of 600 V

IEC 60112, Conditioned

Dielectric constant, 100Hz

23.0 °C

7 [-]

Show Supplier Material materials with Dielectric constant, 100Hz of 7 [-]

IEC 60250

Dielectric constant, 1MHz

23.0 °C

3 [-]

Show Supplier Material materials with Dielectric constant, 1MHz of 3 [-]

IEC 60250

Dielectric strength

23.0 °C

26 kV/mm

Show Supplier Material materials with Dielectric strength of 26 kV/mm

IEC 60243-1, Conditioned

Dissipation factor, 100Hz

23.0 °C

0.19 [-]

Show Supplier Material materials with Dissipation factor, 100Hz of 0.19 [-]

IEC 60250

Dissipation factor, 1MHz

23.0 °C

0.06 [-]

Show Supplier Material materials with Dissipation factor, 1MHz of 0.06 [-]

IEC 60250

Rheological Properties

PropertyValueComment

Melt volume-flow rate

18.5 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 18.5 cm³/10min

ISO 1133, 235°C/2.16kg

Technological properties

Property
Application areas

Main applications:

  • Sports Equipment,Accessories - Tennis racquet bumpers

  • Other

    Packaging:

  • This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

    Shelf Life:

  • Two years from the delivery. For any use above this limit, please refer to our technical services.

  • Processing methods

    Injection Molding:

  • Typical melt temperature (Min / Recommended / Max) : 210°C / 230°C / 280°C.
  • Mold temperature : 20 - 60°C
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80-90°C.