Rilsan® BMNO TLD

Alternative and trade names
PA11
Want to keep this datasheet? Save it now in your required format

Description

PA11, MHLR, 12-010

Rilsan® BMNO TLD resin is a polyamide 11 produced from a renewable source. This natural grade is designed for injection molding. The percentage of renewable carbon according to ASTM D6866 (calculated) is 97%.

This material data has been provided by Arkema High Performance Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Bio-based content

97 %

Show Supplier Material materials with Bio-based content of 97 %

ASTM D6866

Density

23.0 °C

1.03 g/cm³

Show Supplier Material materials with Density of 1.03 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.8 %

Show Supplier Material materials with Moisture absorption of 0.8 %

Sim. to ISO 62

Water absorption

23.0 °C

1.9 %

Show Supplier Material materials with Water absorption of 1.9 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

1.32 GPa

Show Supplier Material materials with Elastic modulus of 1.32 GPa

ISO 527-1/-2, Conditioned

Elongation

23.0 °C

50 %

Show Supplier Material materials with Elongation of 50 %

min., ISO 527-1/-2, nominal, Conditioned

Elongation at yield

23.0 °C

5 %

Show Supplier Material materials with Elongation at yield of 5 %

ISO 527-1/-2, Conditioned

Hardness, Shore D

23.0 °C

68 [-]

Show Supplier Material materials with Hardness, Shore D of 68 [-]

ISO 7619-1, 15 seconds

Yield strength

23.0 °C

41 MPa

Show Supplier Material materials with Yield strength of 41 MPa

ISO 527-1/-2, Conditioned

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

8.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 8.5E-5 1/K

ISO 11359-1/-2

Heat deflection temperature, 0.45 MPa

145 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 145 °C

ISO 75-1/-2

Heat deflection temperature, 1.80 MPa

50 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 50 °C

ISO 75-1/-2

Melting point

189 °C

Show Supplier Material materials with Melting point of 189 °C

ISO 11357-1/-3, 10°C/min

Vicat softening temperature

160 °C

Show Supplier Material materials with Vicat softening temperature of 160 °C

ISO 306, 50°C/h 50N

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Supplier Material materials with Comparative tracking index of 600 V

IEC 60112, Conditioned

Dielectric constant, 100Hz

23.0 °C

4 [-]

Show Supplier Material materials with Dielectric constant, 100Hz of 4 [-]

IEC 60250

Dielectric constant, 1MHz

23.0 °C

3 [-]

Show Supplier Material materials with Dielectric constant, 1MHz of 3 [-]

IEC 60250

Dielectric strength

23.0 °C

30 kV/mm

Show Supplier Material materials with Dielectric strength of 30 kV/mm

IEC 60243-1, Conditioned

Dissipation factor, 100Hz

23.0 °C

0.06 [-]

Show Supplier Material materials with Dissipation factor, 100Hz of 0.06 [-]

IEC 60250

Dissipation factor, 1MHz

23.0 °C

0.03 [-]

Show Supplier Material materials with Dissipation factor, 1MHz of 0.03 [-]

IEC 60250

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

11 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 11 cm³/10min

ISO 1133, 235°C/2.16kg

Shrinkage

23.0 °C

0.4 %

Show Supplier Material materials with Shrinkage of 0.4 %

ISO 294-4 2577

Shrinkage, transverse

23.0 °C

0.8 %

Show Supplier Material materials with Shrinkage, transverse of 0.8 %

ISO 294-4 2577

Technological properties

Property
Application areas

Main applications:

  • Quick connectors parts, Fittings, Components, and Injection Molded Parts
  • Footwear - Outsoles

  • Other

    Packaging:

  • This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

    Shelf Life:

  • Two years from the delivery. For any use above this limit, please refer to our technical services.

  • Processing methods

    Injection Molding:

  • Typical melt temperature (Min / Recommended / Max) : 210°C / 230°C / 280°C.
  • Mold temperature : 20 - 60°C
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80-90°C.