Rilsan® BMVO TLD

Alternative and trade names
Want to keep this datasheet? Save it now in your required format


PA11, MHLR, 18-010

Rilsan® BMVO TLD resin is a polyamide 11 produced from a renewable source. This natural grade is designed for injection molding. The percentage of renewable carbon according to ASTM D6866 (calculated) is 99%.

This material data has been provided by Arkema High Performance Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.




Bio-based content

99 %

Show Supplier Material materials with Bio-based content of 99 %

ASTM D6866


23.0 °C

1.03 g/cm³

Show Supplier Material materials with Density of 1.03 g/cm³

ISO 1183



Elastic modulus

23.0 °C

1.37 GPa

Show Supplier Material materials with Elastic modulus of 1.37 GPa

ISO 527-1/-2, Conditioned


23.0 °C

50 %

Show Supplier Material materials with Elongation of 50 %

min., ISO 527-1/-2, nominal, Conditioned

Elongation at yield

23.0 °C

5 %

Show Supplier Material materials with Elongation at yield of 5 %

ISO 527-1/-2, Conditioned

Hardness, Shore D

23.0 °C

71 [-]

Show Supplier Material materials with Hardness, Shore D of 71 [-]

ISO 7619-1, 15 seconds

Yield strength

23.0 °C

42 MPa

Show Supplier Material materials with Yield strength of 42 MPa

ISO 527-1/-2, Conditioned



Melting point

189 °C

Show Supplier Material materials with Melting point of 189 °C

ISO 11357-1/-3, 10°C/min

Rheological Properties



23.0 °C

0.1 %

Show Supplier Material materials with Shrinkage of 0.1 %

ISO 294-4 2577

Shrinkage, transverse

23.0 °C

1 %

Show Supplier Material materials with Shrinkage, transverse of 1 %

ISO 294-4 2577

Technological properties

Application areas

Main applications:

  • Quick connectors parts
  • Pneumatic Tubing

  • Other


  • This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

    Shelf Life:

  • Two years from the delivery. For any use above this limit, please refer to our technical services.

  • Processing methods

    Injection Molding:

  • Typical melt temperature (Min / Recommended / Max) : 230°C / 250°C / 270°C.
  • Mold temperature : 20 - 60°C
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80-90°C.