Rilsan® BZM 23 G9

Alternative and trade names
PA11-(GF+CD)30
Want to keep this datasheet? Save it now in your required format

Description

PA11, MRS, 18-060, GF 23 + CD

Rilsan® BZM 23 G9 is a fiberglass reinforced polyamide 11 produced from a renewable source. This black grade with improved friction properties is designed for injection molding. The percentage of renewable carbon according to ASTM D6866 (calculated) is 86%.

This material data has been provided by Arkema Technical Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting Standard

Bio-based content

86 %

Show Supplier Material materials with Bio-based content of 86 %

Density

1.22 g/cm³

Show Supplier Material materials with Density of 1.22 g/cm³

dry

ISO 1183

Limiting oxygen index

22 %

Show Supplier Material materials with Limiting oxygen index of 22 %

dry

ISO 4589-1/-2

Water absorption

1.2 %

Show Supplier Material materials with Water absorption of 1.2 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

6.1 GPa

Show Supplier Material materials with Elastic modulus of 6.1 GPa

cond.

ISO 527-1/-2

Elongation

5 %

Show Supplier Material materials with Elongation of 5 %

cond.

ISO 527-1/-2

Hardness, Shore D

74 [-]

Show Supplier Material materials with Hardness, Shore D of 74 [-]

dry

ISO 7619-1

15 seconds

Impact strength, Charpy notched

-30 °C

10 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m²

cond.

ISO 179/1eA

23 °C

13 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 13 kJ/m²

cond.

ISO 179/1eA

Impact strength, Charpy unnotched

-30 °C

83 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 83 kJ/m²

cond.

ISO 179/1eU

23 °C

74 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 74 kJ/m²

cond.

ISO 179/1eU

Unlock all property charts

Tensile strength

108 MPa

Show Supplier Material materials with Tensile strength of 108 MPa

cond.

ISO 527-1/-2

Thermal

PropertyValueConditionTesting StandardComment

Coefficient of thermal expansion

5e-05 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 5e-05 1/K

dry

ISO 11359-1/-2

Melting point

186 °C

Show Supplier Material materials with Melting point of 186 °C

dry

ISO 11357-1/-3

10°C/min

Vicat softening temperature

170 °C

Show Supplier Material materials with Vicat softening temperature of 170 °C

ISO 306

50°C/h 50N

Flammability

At thickness 1.6 mm IEC 60695-11-10: HB, At thickness 3.2 mm IEC 60695-11-10: HB

Electrical

PropertyValueConditionTesting StandardFrequency

Comparative tracking index

300 V

Show Supplier Material materials with Comparative tracking index of 300 V

cond.

IEC 60112

Dielectric constant

5 [-]

Show Supplier Material materials with Dielectric constant of 5 [-]

dry

IEC 60250

100Hz

5 [-]

Show Supplier Material materials with Dielectric constant of 5 [-]

dry

IEC 60250

1MHz

Dielectric strength

22 kV/mm

Show Supplier Material materials with Dielectric strength of 22 kV/mm

cond.

IEC 60243-1

Dissipation factor

0.0208 [-]

Show Supplier Material materials with Dissipation factor of 0.0208 [-]

dry

IEC 60250

1MHz

0.0334 [-]

Show Supplier Material materials with Dissipation factor of 0.0334 [-]

dry

IEC 60250

100Hz

Surface resistivity

6e+12 Ω/sq

Show Supplier Material materials with Surface resistivity of 6e+12 Ω/sq

cond.

IEC 60093

Volume resistivity

2e+11 Ω·cm

Show Supplier Material materials with Volume resistivity of 2e+11 Ω·cm

cond.

IEC 60093

Rheological Properties

PropertyValueConditionTesting StandardComment

Melt volume-flow rate

9 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 9 cm³/10min

dry

ISO 1133

235°C/5kg

Technological properties

Property
Application areas

Chemical Process Industry - Injection Molding

Fillers

30% Glass Fiber and Carbon Black

Processing methods

Injection Molding:

  • Typical melt temperature (Min / Recommended / Max) : 250°C / 270°C / 290°C.
  • Mold temperature : 40 - 90°C
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80-90°C.