Rilsan® BZM 30 BLACK TL

Alternative and trade names
PA11-GF30

Want to keep this datasheet? Save it now in your required format

Description

PA11,MHL,18-070,GF30

Rilsan® BZM 30 BLACK TLis a fiberglass reinforced polyamide 11 produced from a renewable source. This black grade is designed for injection molding. The percentage of renewable carbon according to ASTM D6866 (calculated) is 95%.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Condition	Testing Standard
Bio-based content	95 % Show Supplier Material materials with Bio-based content of 95 %
Density	1.25 g/cm³ Show Supplier Material materials with Density of 1.25 g/cm³	dry	ISO 1183
Water absorption	1.3 % Show Supplier Material materials with Water absorption of 1.3 %		Sim. to ISO 62

Mechanical

Property	Temperature	Value	Condition	Testing Standard	Comment
Elastic modulus		6.9 GPa Show Supplier Material materials with Elastic modulus of 6.9 GPa	cond.	ISO 527-1/-2
Elongation		6 % Show Supplier Material materials with Elongation of 6 %	cond.	ISO 527-1/-2
Hardness, Shore D		74 [-] Show Supplier Material materials with Hardness, Shore D of 74 [-]	dry	ISO 7619-1	15 seconds
Impact strength, Charpy notched	-30 °C	11 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²	cond.	ISO 179/1eA
	23 °C	20 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 20 kJ/m²	cond.	ISO 179/1eA
Impact strength, Charpy unnotched	-30 °C	83 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 83 kJ/m²	cond.	ISO 179/1eU
	23 °C	74 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 74 kJ/m²	cond.	ISO 179/1eU
Tensile strength		110 MPa Show Supplier Material materials with Tensile strength of 110 MPa	cond.	ISO 527-1/-2

Thermal

Property	Value	Condition	Testing Standard	Comment
Melting point	189 °C Show Supplier Material materials with Melting point of 189 °C	dry	ISO 11357-1/-3	10°C/min

Rheological Properties

Property	Value	Condition	Testing Standard	Comment
Melt volume-flow rate	7 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 7 cm³/10min	dry	ISO 1133	235°C/5kg

Technological properties

Property

Application areas

Connectors

Fillers

30% Glass Fiber

Processing methods

Injection Molding:

Typical melt temperature (Min / Recommended / Max) : 250°C / 270°C / 290°C.

Mold temperature : 40 - 90°C

Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80-90°C.