General
Property | Value | Condition | Testing Standard |
---|---|---|---|
Bio-based content | 97 % Show Supplier Material materials with Bio-based content of 97 % | ||
Density | 1.25 g/cm³ Show Supplier Material materials with Density of 1.25 g/cm³ | dry | ISO 1183 |
Limiting oxygen index | 22 % Show Supplier Material materials with Limiting oxygen index of 22 % | dry | ISO 4589-1/-2 |
Moisture absorption | 0.5 % Show Supplier Material materials with Moisture absorption of 0.5 % | Sim. to ISO 62 | |
Water absorption | 1.4 % Show Supplier Material materials with Water absorption of 1.4 % | Sim. to ISO 62 |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elastic modulus | 7.3 GPa Show Supplier Material materials with Elastic modulus of 7.3 GPa | cond. | ISO 527-1/-2 | ||
Elongation | 6 % Show Supplier Material materials with Elongation of 6 % | cond. | ISO 527-1/-2 | ||
Hardness, Shore D | 74 [-] Show Supplier Material materials with Hardness, Shore D of 74 [-] | dry | ISO 7619-1 | 15 seconds | |
Impact strength, Charpy notched | -30 °C | 17 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 17 kJ/m² | cond. | ISO 179/1eA | |
23 °C | 24 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 24 kJ/m² | cond. | ISO 179/1eA | ||
Impact strength, Charpy unnotched | -30 °C | 96 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 96 kJ/m² | cond. | ISO 179/1eU | |
23 °C | 89 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 89 kJ/m² | cond. | ISO 179/1eU | ||
Tensile strength | 117 MPa Show Supplier Material materials with Tensile strength of 117 MPa | cond. | ISO 527-1/-2 |
Thermal
Property | Value | Condition | Testing Standard | Comment | |||
---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 5e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5e-05 1/K | dry | ISO 11359-1/-2 | ||||
Melting point | 189 °C Show Supplier Material materials with Melting point of 189 °C | dry | ISO 11357-1/-3 | 10°C/min | |||
Vicat softening temperature | 170 °C Show Supplier Material materials with Vicat softening temperature of 170 °C | ISO 306 | 50°C/h 50N | ||||
Flammability | At thickness 1.6 mm IEC 60695-11-10: HB, At thickness 3.2 mm IEC 60695-11-10: HB |
Electrical
Property | Value | Condition | Testing Standard | Frequency |
---|---|---|---|---|
Comparative tracking index | 600 V Show Supplier Material materials with Comparative tracking index of 600 V | cond. | IEC 60112 | |
Dielectric constant | 4 [-] Show Supplier Material materials with Dielectric constant of 4 [-] | dry | IEC 60250 | 100Hz |
4 [-] Show Supplier Material materials with Dielectric constant of 4 [-] | dry | IEC 60250 | 1MHz | |
Dielectric strength | 45 kV/mm Show Supplier Material materials with Dielectric strength of 45 kV/mm | cond. | IEC 60243-1 | |
Dissipation factor | 0.021 [-] Show Supplier Material materials with Dissipation factor of 0.021 [-] | dry | IEC 60250 | 1MHz |
0.0578 [-] Show Supplier Material materials with Dissipation factor of 0.0578 [-] | dry | IEC 60250 | 100Hz | |
Surface resistivity | 1e+14 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+14 Ω/sq | cond. | IEC 60093 | |
Volume resistivity | 7e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 7e+11 Ω·cm | cond. | IEC 60093 |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Melt volume-flow rate | 9 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 9 cm³/10min | dry | ISO 1133 | 235°C/5kg |
Technological properties
Property | ||
---|---|---|
Application areas | Connectors,Footwear - Outsoles,Sports Equipment | |
Fillers | 30% Glass Fiber | |
Processing methods | Injection Molding: |