Rilsan® BZM 7 O TL

Alternative and trade names
PA11-GF8

Want to keep this datasheet? Save it now in your required format

Description

PA11, MHLR, 18-030, GF8

Rilsan® BZM 7 O TL is a fiberglass reinforced polyamide 11 produced from a renewable source. This natural grade is designed for injection. The percentage of renewable carbon according to ASTM D6866 (calculated) is 97%.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Condition	Testing Standard
Bio-based content	97 % Show Supplier Material materials with Bio-based content of 97 %
Density	1.07 g/cm³ Show Supplier Material materials with Density of 1.07 g/cm³	dry	ISO 1183

Mechanical

Property	Temperature	Value	Condition	Testing Standard	Comment
Elastic modulus		1.8 GPa Show Supplier Material materials with Elastic modulus of 1.8 GPa	cond.	ISO 527-1/-2
Elongation		50 % Show Supplier Material materials with Elongation of 50 %	cond.	ISO 527-1/-2	min. \| nominal
Elongation at yield		7 % Show Supplier Material materials with Elongation at yield of 7 %	cond.	ISO 527-1/-2
Hardness, Shore D		71 [-] Show Supplier Material materials with Hardness, Shore D of 71 [-]	dry	ISO 7619-1	15 seconds
Impact strength, Charpy notched	-30 °C	12 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m²	cond.	ISO 179/1eA
	23 °C	22 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 22 kJ/m²	cond.	ISO 179/1eA

Thermal

Property	Value	Condition	Testing Standard	Comment
Melting point	189 °C Show Supplier Material materials with Melting point of 189 °C	dry	ISO 11357-1/-3	10°C/min

Rheological Properties

Property	Value	Condition	Testing Standard	Comment
Melt volume-flow rate	20 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 20 cm³/10min	dry	ISO 1133	235°C/5kg
Shrinkage	0.6 % Show Supplier Material materials with Shrinkage of 0.6 %	dry	ISO 294-4
	1 % Show Supplier Material materials with Shrinkage of 1 %	dry	ISO 294-4	Transverse

Technological properties

Property

Application areas

Main applications:

Spring for quick connectors

Outsoles

Packaging: This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

Shelf life: Two years from the delivery. For any use above this limit, please refer to our technical services.

Fillers

8% Glass Fiber

Processing methods

Injection Molding:

Typical melt temperature (Min / Recommended / Max) : 250°C / 270°C / 290°C.

Mold temperature : 40 - 90°C

Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80-90°C.