General
Property | Value | Condition | Testing Standard |
---|---|---|---|
Density | 1.05 g/cm³ Show Supplier Material materials with Density of 1.05 g/cm³ | dry | ISO 1183 |
Limiting oxygen index | 26 % Show Supplier Material materials with Limiting oxygen index of 26 % | dry | ISO 4589-1/-2 |
Moisture absorption | 1.7 % Show Supplier Material materials with Moisture absorption of 1.7 % | Sim. to ISO 62 | |
Water absorption | 3.8 % Show Supplier Material materials with Water absorption of 3.8 % | Sim. to ISO 62 |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elastic modulus | 2.0 GPa Show Supplier Material materials with Elastic modulus of 2.0 GPa | cond. | ISO 527-1/-2 | ||
2.1 GPa Show Supplier Material materials with Elastic modulus of 2.1 GPa | dry | ISO 527-1/-2 | |||
Elongation | 50 % Show Supplier Material materials with Elongation of 50 % | cond., dry | ISO 527-1/-2 | min. | nominal | |
Elongation at yield | 8 % Show Supplier Material materials with Elongation at yield of 8 % | dry | ISO 527-1/-2 | ||
9 % Show Supplier Material materials with Elongation at yield of 9 % | cond. | ISO 527-1/-2 | |||
Hardness, Shore D | 79 [-] Show Supplier Material materials with Hardness, Shore D of 79 [-] | dry | ISO 7619-1 | 15 seconds | |
Impact strength, Charpy notched | -30 °C | 13 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 13 kJ/m² | cond. | ISO 179/1eA | |
23 °C | 13 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 13 kJ/m² | cond. | ISO 179/1eA | ||
Impact strength, Charpy unnotched | No Break at -30°C | dry and cond. | ISO 179/1eU | ||
Yield strength | 61 MPa Show Supplier Material materials with Yield strength of 61 MPa | cond. | ISO 527-1/-2 |
Thermal
Property | Value | Condition | Testing Standard | Comment | |||
---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 7e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7e-05 1/K | dry | ISO 11359-1/-2 | ||||
Glass transition temperature | 168 °C Show Supplier Material materials with Glass transition temperature of 168 °C | dry | ISO 11357-1/-2 | 10°C/min | |||
Vicat softening temperature | 160 °C Show Supplier Material materials with Vicat softening temperature of 160 °C | ISO 306 | 50°C/h 50N | ||||
Flammability | At thickness 1.6 mm IEC 60695-11-10: HV-2, At thickness 0.8 mm IEC 60695-11-10: HB |
Electrical
Property | Value | Condition | Testing Standard |
---|---|---|---|
Comparative tracking index | 600 V Show Supplier Material materials with Comparative tracking index of 600 V | cond. | IEC 60112 |
Dielectric strength | 50 kV/mm Show Supplier Material materials with Dielectric strength of 50 kV/mm | cond. | IEC 60243-1 |
Surface resistivity | 1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | cond. | IEC 60093 |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | cond. | IEC 60093 |
Optical
Property | Value | Testing Standard |
---|---|---|
Luminous transmittance | 91 [-] Show Supplier Material materials with Luminous transmittance of 91 [-] | ISO 13468-1/2 |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Melt volume-flow rate | 2 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 2 cm³/10min | dry | ISO 1133 | 275°C/2.16kg |
Shrinkage | 0.7 % Show Supplier Material materials with Shrinkage of 0.7 % | dry | ISO 294-4 | |
0.7 % Show Supplier Material materials with Shrinkage of 0.7 % | dry | ISO 294-4 | Transverse |
Technological properties
Property | ||
---|---|---|
Application areas | Breathing Masks,Healthcare-Other | |
Certifications | USP Class VI | |
Processing methods | Injection Molding: Film Extrusion: |