Rilsan® HT CESV BLACK P010 TL

Alternative and trade names
PA*-I
Want to keep this datasheet? Save it now in your required format

Description

PA11/10T-I,,EHL,C16-010

Rilsan® HT CESV BLACK P010 TL

is a flexible polyphthalamide produced from a renewable source, typical used to replace metal in tubing for high-temperature automotive, transportation and other demanding technical applications. Percentage of renewable carbon according to ASTM D6866: 45 %.

This material data has been provided by Arkema High Performance Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Bio-based content

45 %

Show Supplier Material materials with Bio-based content of 45 %

ASTM D6866

Density

23.0 °C

1.05 g/cm³

Show Supplier Material materials with Density of 1.05 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

1.02 GPa

Show Supplier Material materials with Elastic modulus of 1.02 GPa

ISO 527-1/-2, Conditioned

Elongation

23.0 °C

50 %

Show Supplier Material materials with Elongation of 50 %

min., ISO 527-1/-2, nominal, Conditioned

Elongation at yield

23.0 °C

5 %

Show Supplier Material materials with Elongation at yield of 5 %

ISO 527-1/-2, Conditioned

Hardness, Shore D

23.0 °C

66 [-]

Show Supplier Material materials with Hardness, Shore D of 66 [-]

ISO 7619-1, 15 seconds

Yield strength

23.0 °C

30 MPa

Show Supplier Material materials with Yield strength of 30 MPa

ISO 527-1/-2, Conditioned

Thermal

PropertyValueComment

Glass transition temperature

82 °C

Show Supplier Material materials with Glass transition temperature of 82 °C

ISO 11357-1/-2, 10°C/min

Heat deflection temperature, 0.45 MPa

82 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 82 °C

ISO 75-1/-2

Heat deflection temperature, 1.80 MPa

66 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 66 °C

ISO 75-1/-2

Melting point

260 °C

Show Supplier Material materials with Melting point of 260 °C

ISO 11357-1/-3, 10°C/min

Rheological Properties

PropertyValueComment

Melt volume-flow rate

1.9 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 1.9 cm³/10min

ISO 1133, 300°C/5kg

Technological properties

Property
Application areas

Main applications:

  • Thermoplastic lines for automotive; transportation applications such as high temperature air/vacuum
  • Aggressive media and oil management systems
  • Cooling and selective catalyst reduction lines etc
  • Hydraulic and pneumatic lines
  • Auto - Water Cooling Circuit,
  • Emission Control Systems - Air Conditioning Circuit, Vacuum and Blow by Lines
  • Fluid Management - Brakebooster Lines, Transmission oil Cooling Circuit

  • Other

    Packaging:

  • This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

    Shelf Life:

  • Two years from the delivery. For any use above this limit, please refer to our technical services.

  • Processing methods

    Profile Extrusion:

  • Typical melt temperature (Min / Recommended / Max) : 270°C / 280°C / 290°C.** **
  • Drying time and temperature (only for bags opened for more than two hours) : 8 - 12 hours at 70 °C.