Rilsan® HT CSR13

Alternative and trade names
PA*-CF15
Want to keep this datasheet? Save it now in your required format

Description

PA11/10T,CF13,MHL, C16-080 Rilsan® HT CSR 13 is a flexible polyphthalamide produced from a renewable source. This grade is fiber reinforced formulated for high-temperature applications requiring static charge dissipation and designed for injection molding. Percentage of renewable carbon according to ASTM D6866: 53%.

This material data has been provided by Arkema Technical Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting Standard

Bio-based content

53 %

Show Supplier Material materials with Bio-based content of 53 %

Density

1.15 g/cm³

Show Supplier Material materials with Density of 1.15 g/cm³

dry

ISO 1183

Mechanical

PropertyTemperatureValueConditionTesting Standard

Elastic modulus

7.6 GPa

Show Supplier Material materials with Elastic modulus of 7.6 GPa

cond.

ISO 527-1/-2

Elongation

2 %

Show Supplier Material materials with Elongation of 2 %

cond.

ISO 527-1/-2

Impact strength, Charpy notched

-30 °C

4 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 4 kJ/m²

cond.

ISO 179/1eA

23 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 5 kJ/m²

cond.

ISO 179/1eA

Impact strength, Charpy unnotched

-30 °C

32 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 32 kJ/m²

cond.

ISO 179/1eU

23 °C

40 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 40 kJ/m²

cond.

ISO 179/1eU

Unlock all property charts

Tensile strength

151 MPa

Show Supplier Material materials with Tensile strength of 151 MPa

cond.

ISO 527-1/-2

Yield strength

37 MPa

Show Supplier Material materials with Yield strength of 37 MPa

dry

ISO 527-1/-2

Thermal

PropertyValueConditionTesting StandardComment

Melting point

255 °C

Show Supplier Material materials with Melting point of 255 °C

dry

ISO 11357-1/-3

10°C/min

Rheological Properties

PropertyValueConditionTesting StandardComment

Melt volume-flow rate

12 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 12 cm³/10min

dry

ISO 1133

275°C/2.16kg

Technological properties

Property
Application areas

Connectors

Fillers

15% Carbon Fiber

Processing methods

Injection Molding:

  • Typical melt temperature (Min / Recommanded / Maxi) : 270°C / 280°C / 320°C.
  • Typical mold temperature : 80 - 110°C.
  • Drying time and temperature (only for bags opened for more than two hours) : 4 - 8 hours / 100 - 110°C.