Rilsan® HT CZM 30 BLACK TLD

Alternative and trade names
PA*-GF30

Want to keep this datasheet? Save it now in your required format

Description

PA11/10T,GF30,MHL,C16-090 Rilsan® HT CZM 30 BLACK TLD

is a polyphthalamide produced from a renewable source. This grade is glass fiber-reinforced, formulated and designed for injection molding for high-temperature applications. Percentage of renewable carbon according to ASTM D6866: 67%.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Condition	Testing Standard
Bio-based content	67 % Show Supplier Material materials with Bio-based content of 67 %
Density	1.3 g/cm³ Show Supplier Material materials with Density of 1.3 g/cm³	dry	ISO 1183
Moisture absorption	0.22 % Show Supplier Material materials with Moisture absorption of 0.22 %		Sim. to ISO 62
Water absorption	1.13 % Show Supplier Material materials with Water absorption of 1.13 %		Sim. to ISO 62

Mechanical

Property	Temperature	Value	Condition	Testing Standard	Comment
Elastic modulus		8.5 GPa Show Supplier Material materials with Elastic modulus of 8.5 GPa	cond.	ISO 527-1/-2
Elongation		4 % Show Supplier Material materials with Elongation of 4 %	cond.	ISO 527-1/-2
Hardness, Shore D		83 [-] Show Supplier Material materials with Hardness, Shore D of 83 [-]	dry	ISO 7619-1	15 seconds
Impact strength, Charpy unnotched	-30 °C	46 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 46 kJ/m²	cond.	ISO 179/1eU
	23 °C	51 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 51 kJ/m²	cond.	ISO 179/1eU
Tensile strength		130 MPa Show Supplier Material materials with Tensile strength of 130 MPa	cond.	ISO 527-1/-2
Yield strength		45 MPa Show Supplier Material materials with Yield strength of 45 MPa	dry	ISO 527-1/-2

Thermal

Property	Value	Condition	Testing Standard	Comment
Glass transition temperature	75 °C Show Supplier Material materials with Glass transition temperature of 75 °C	dry	ISO 11357-1/-2	10°C/min
Melting point	255 °C Show Supplier Material materials with Melting point of 255 °C	dry	ISO 11357-1/-3	10°C/min

Rheological Properties

Property	Value	Condition	Testing Standard	Comment
Melt volume-flow rate	15 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 15 cm³/10min	dry	ISO 1133	300°C/2.16kg

Technological properties

Property

Application areas

Connectors,Auto - Water Cooling Circuit

Fillers

30% Glass Fiber

Processing methods

Injection Molding:

Typical melt temperature (Min / Recommanded / Maxi) : 270°C / 280°C / 320°C.

Typical mold temperature : 90 - 110°C.

Drying time and temperature (only for bags opened for more than two hours) : 4 - 8 hours / 100 - 110°C.

Rilsan® HT CZM 30 BLACK TLD

Description

Ashby charts

Applications

Materials by this supplier

Properties