Rilsan® MB 3610 NAT

Alternative and trade names
PA11-I
Want to keep this datasheet? Save it now in your required format

Description

PA11-P, EHL, 22-002

Rilsan® MB 3610 NAT resin is a polyamide 11 produced from a renewable source. This natural grade is plasticized and specially designed for pneumatic applications. It combines very high flexibility with good impact resistance. The percentage of renewable carbon according to ASTM D6866 (calculated) is 59%.

This material data has been provided by Arkema Technical Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting Standard

Bio-based content

59 %

Show Supplier Material materials with Bio-based content of 59 %

Density

1.03 g/cm³

Show Supplier Material materials with Density of 1.03 g/cm³

dry

ISO 1183

Moisture absorption

0.45 %

Show Supplier Material materials with Moisture absorption of 0.45 %

Sim. to ISO 62

Water absorption

1.1 %

Show Supplier Material materials with Water absorption of 1.1 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

0.21 GPa

Show Supplier Material materials with Elastic modulus of 0.21 GPa

cond.

ISO 527-1/-2

Hardness, Shore D

53 [-]

Show Supplier Material materials with Hardness, Shore D of 53 [-]

dry

ISO 7619-1

15 seconds

Impact strength, Charpy notched

-30 °C

10 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m²

cond.

ISO 179/1eA

No Break at 23°C

Impact strength, Charpy unnotched

No Break at 23 and -30°C

cond.

ISO 179/1eU

Thermal

PropertyValueConditionTesting StandardComment

Melting point

188 °C

Show Supplier Material materials with Melting point of 188 °C

dry

ISO 11357-1/-3

10°C/min

Electrical

PropertyValueConditionTesting Standard

Volume resistivity

1.9e+13 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.9e+13 Ω·cm

dry

IEC 60093

Rheological Properties

PropertyValueConditionTesting StandardComment

Melt volume-flow rate

4 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 4 cm³/10min

dry

ISO 1133

235°C/5kg

Technological properties

Property
Application areas

Main applications:

  • Pneumatic tubing

    Packaging: This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

    Shelf life: Two years from the delivery. For any use above this limit, please refer to our technical services.

  • Processing methods

    Extrusion:

  • Typical melt temperature (Min / Recommended / Max) : 230°C / 250°C / 280°C.
  • Drying time and temperature (only necessary for bags opened for more than two hours) : 4-8 hours at 80-90°C.