Rilsan® SZM 30 BLACK TL

Alternative and trade names
PA610-GF30
Want to keep this datasheet? Save it now in your required format

Description

Rilsan® SZM 30 BLACK TL resin

  • Rilsan® POLYAMIDE 610 (PA610)

    Rilsan® SZM 30 BLACK TL is a stabilized Polyamide 610 resin reinforced with 30% glass fiber. This grade is designed for injection molding application. Percentage of renewable carbon according to ASTM D6866: 60%.

  • This material data has been provided by Arkema High Performance Polymers.

    All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
    Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

    Ashby charts

    See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

    Properties

    General

    PropertyTemperatureValueComment

    Bio-based content

    60 %

    Show Supplier Material materials with Bio-based content of 60 %

    ASTM D6866

    Density

    23.0 °C

    1.31 g/cm³

    Show Supplier Material materials with Density of 1.31 g/cm³

    ISO 1183

    Mechanical

    PropertyTemperatureValueComment

    Elastic modulus

    23.0 °C

    8.3 GPa

    Show Supplier Material materials with Elastic modulus of 8.3 GPa

    ISO 527-1/-2

    Impact strength, Charpy notched

    -30.0 °C

    10 kJ/m²

    Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m²

    23.0 °C

    16 kJ/m²

    Show Supplier Material materials with Impact strength, Charpy notched of 16 kJ/m²

    Impact strength, Charpy unnotched

    -30.0 °C

    89 kJ/m²

    Show Supplier Material materials with Impact strength, Charpy unnotched of 89 kJ/m²

    ISO 179/1eU

    23.0 °C

    90 kJ/m²

    Show Supplier Material materials with Impact strength, Charpy unnotched of 90 kJ/m²

    ISO 179/1eU

    Unlock all property charts

    Thermal

    PropertyValueComment

    Heat deflection temperature, 0.45 MPa

    221 °C

    Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 221 °C

    ISO 75-1/-2

    Heat deflection temperature, 1.80 MPa

    210 °C

    Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 210 °C

    ISO 75-1/-2

    Melting point

    222 °C

    Show Supplier Material materials with Melting point of 222 °C

    ISO 11357-1/-3, 10°C/min

    Vicat softening temperature

    217 °C

    Show Supplier Material materials with Vicat softening temperature of 217 °C

    ISO 306, 50°C/h 50N

    Rheological Properties

    PropertyTemperatureValueComment

    Shrinkage

    23.0 °C

    0.5 %

    Show Supplier Material materials with Shrinkage of 0.5 %

    ISO 294-4 2577

    Shrinkage, transverse

    23.0 °C

    1 %

    Show Supplier Material materials with Shrinkage, transverse of 1 %

    ISO 294-4 2577

    Technological properties

    Property
    Fillers

    30% Glass Fiber