Rilsan® SZM 30 O TL

Alternative and trade names
PA610-GF30

Want to keep this datasheet? Save it now in your required format

Description

Rilsan® SZM 30 O TL resin

Rilsan® POLYAMIDE 610 (PA610)

Rilsan® SZM 30 O TL is a stabilized polyamide 610 resin reinforced with 30% glass fiber. This grade is designed for injection molding application. Percentage of renewable carbon according to ASTM D6866: 60%.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Condition	Testing Standard
Bio-based content	60 % Show Supplier Material materials with Bio-based content of 60 %
Density	1.31 g/cm³ Show Supplier Material materials with Density of 1.31 g/cm³	dry	ISO 1183

Mechanical

Property	Temperature	Value	Condition	Testing Standard
Elastic modulus		8.3 GPa Show Supplier Material materials with Elastic modulus of 8.3 GPa	dry	ISO 527-1/-2
Elongation		5 % Show Supplier Material materials with Elongation of 5 %	dry	ISO 527-1/-2
Impact strength, Charpy notched	-30 °C	10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m²	dry	ISO 179/1eA
	23 °C	16 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 16 kJ/m²	dry	ISO 179/1eA
Impact strength, Charpy unnotched	-30 °C	89 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 89 kJ/m²	dry	ISO 179/1eU
	23 °C	90 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 90 kJ/m²	dry	ISO 179/1eU
Tensile strength		150 MPa Show Supplier Material materials with Tensile strength of 150 MPa	dry	ISO 527-1/-2

Thermal

Property	Value	Condition	Testing Standard	Comment
Melting point	222 °C Show Supplier Material materials with Melting point of 222 °C	dry	ISO 11357-1/-3	10°C/min
Vicat softening temperature	217 °C Show Supplier Material materials with Vicat softening temperature of 217 °C		ISO 306	50°C/h 50N

Rheological Properties

Property	Value	Condition	Testing Standard	Comment
Shrinkage	0.5 % Show Supplier Material materials with Shrinkage of 0.5 %	dry	ISO 294-4
	1 % Show Supplier Material materials with Shrinkage of 1 %	dry	ISO 294-4	Transverse

Technological properties

Property

Application areas

Chemical Process Industry - Stock Shapes

Fillers

30% Glass Fiber

Rilsan® SZM 30 O TL

Description

Ashby charts

Applications

Materials by this supplier

Properties