Rilsan® TESNO F

Alternative and trade names
PA1010
Want to keep this datasheet? Save it now in your required format

Description

Rilsan® TESNO F resin Rilsan® POLYAMIDE 1010 (PA1010)

Rilsan® TESNO F resin is an undried polyamide 1010 neat resin produced from a renewable source. This natural grade is a designed for compounding. Percentage of renewable carbon according to ASTM D6866: 99%.

This material data has been provided by Arkema Technical Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting Standard

Bio-based content

99 %

Show Supplier Material materials with Bio-based content of 99 %

Density

1.04 g/cm³

Show Supplier Material materials with Density of 1.04 g/cm³

dry

ISO 1183

Mechanical

PropertyTemperatureValueConditionTesting Standard

Elastic modulus

1.6 GPa

Show Supplier Material materials with Elastic modulus of 1.6 GPa

dry

ISO 527-1/-2

Impact strength, Charpy notched

-30 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²

dry

ISO 179/1eA

23 °C

16 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 16 kJ/m²

dry

ISO 179/1eA

Impact strength, Charpy unnotched

No Break at 23 and -30°C

dry

ISO 179/1eU

Yield strength

29 MPa

Show Supplier Material materials with Yield strength of 29 MPa

cond.

ISO 527-1/-2

Thermal

PropertyValueConditionTesting StandardComment

Melting point

202 °C

Show Supplier Material materials with Melting point of 202 °C

dry

ISO 11357-1/-3

10°C/min

Technological properties

Property
Application areas

Monofilaments