Rilsan® TIEFLEX S452 BLACK T6L

Alternative and trade names
PA*

Want to keep this datasheet? Save it now in your required format

Description

Rilsan® TIEFLEX S452 BLACK T6L resin is a flexible tie layer alloy partially based on renewable resources. This grade is designed for multilayer automotive and trucks fuel lines (tie layer for fuel line). In the case of direct contact with fuel, contact Arkema representative for recommendations.

Packaging:

This grade is delivered dried in sealed packaging (25kg bags) ready to be processed.

Shelf life:

Two years from the date of delivery. For any use above this limit, please refer to our technical services.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Condition	Testing Standard
Density	1.09 g/cm³ Show Supplier Material materials with Density of 1.09 g/cm³	dry	ISO 1183
Moisture absorption	1.2 % Show Supplier Material materials with Moisture absorption of 1.2 %		Sim. to ISO 62
Water absorption	2.9 % Show Supplier Material materials with Water absorption of 2.9 %		Sim. to ISO 62

Mechanical

Property	Temperature	Value	Condition	Testing Standard	Comment
Elastic modulus		0.515 GPa Show Supplier Material materials with Elastic modulus of 0.515 GPa	cond.	ISO 527-1/-2
		0.685 GPa Show Supplier Material materials with Elastic modulus of 0.685 GPa	dry	ISO 527-1/-2
Elongation		50 % Show Supplier Material materials with Elongation of 50 %	cond.	ISO 527-1/-2	min. \| nominal
Elongation at yield		31 % Show Supplier Material materials with Elongation at yield of 31 %	cond.	ISO 527-1/-2
Impact strength, Charpy notched	-30 °C	6.5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 6.5 kJ/m²	cond.	ISO 179/1eA
	23 °C	95 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 95 kJ/m²	cond.	ISO 179/1eA
Impact strength, Charpy unnotched		No Break at 23 and -30°C	cond.	ISO 179/1eU
Yield strength		33 MPa Show Supplier Material materials with Yield strength of 33 MPa	cond.	ISO 527-1/-2

Thermal

Property	Value	Condition	Testing Standard	Comment
Melting point	217 °C Show Supplier Material materials with Melting point of 217 °C	dry	ISO 11357-1/-3	10°C/min

Rheological Properties

Property	Value	Condition	Testing Standard	Comment
Melt volume-flow rate	3.4 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 3.4 cm³/10min	dry	ISO 1133	235°C/5kg

Technological properties

Property

Processing methods

Extrusion:

Typical melt temperature (min / recommended / max): 220°C / 230°C / 270°C

Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 80°C