Rilsan® TMNO

Alternative and trade names
PA1010

Want to keep this datasheet? Save it now in your required format

Description

PA1010, M,22-020

Rilsan® TMNO resin is a dried polyamide 1010 resin neat produced from a renewable source. This natural grade is a designed for compounding, filament extrusion and some injection molding applications. The percentage of renewable carbon according to ASTM D6866 (calculated) is 99%.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Condition	Testing Standard
Bio-based content	99 % Show Supplier Material materials with Bio-based content of 99 %
Density	1.04 g/cm³ Show Supplier Material materials with Density of 1.04 g/cm³	dry	ISO 1183

Mechanical

Property	Temperature	Value	Condition	Testing Standard
Elastic modulus		1.5 GPa Show Supplier Material materials with Elastic modulus of 1.5 GPa	cond.	ISO 527-1/-2
Impact strength, Charpy notched	-30 °C	8 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 8 kJ/m²	cond.	ISO 179/1eA
	23 °C	11 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²	cond.	ISO 179/1eA
Impact strength, Charpy unnotched		No Break at 23 and -30°C	cond.	ISO 179/1eU

Thermal

Property	Value	Condition	Testing Standard	Comment
Melting point	202 °C Show Supplier Material materials with Melting point of 202 °C	dry	ISO 11357-1/-3	10°C/min

Technological properties

Property

Application areas

Main applications:

Monofilament extrusion

Injection molding

Packaging: This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

Shelf life: Two years from the delivery. For any use above this limit, please refer to our technical services.

Processing methods

Injection Molding:

Typical melt temperature (Min / Recommended / Max) : 220°C / 240°C / 280°C.

Mold temperature: 20-60°C

Drying time and temperature (only necessary for bags opened for more than two hours) : 4 hours at 80-90°C.

Extrusion:

Typical melt temperature (Min / Recommended / Max) : 210°C / 230°C / 260°C.