General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 2.84 g/cm³ Show Supplier Material materials with Density of 2.84 g/cm³ |
Surface roughness | 0.4 μm Show Supplier Material materials with Surface roughness of 0.4 μm |
Dimension
Property | Value |
---|---|
Thickness | 100 - 700 mm Show Supplier Material materials with Thickness of 100 - 700 mm |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 23.0 °C | 73.8 GPa Show Supplier Material materials with Elastic modulus of 73.8 GPa |
Elongation A50 | 23.0 °C | 1.5 - 7.7 % Show Supplier Material materials with Elongation A50 of 1.5 - 7.7 % |
Hardness, HBW | 23.0 °C | 130 [-] Show Supplier Material materials with Hardness, HBW of 130 [-] |
Tensile strength | 23.0 °C | 399 - 457 MPa Show Supplier Material materials with Tensile strength of 399 - 457 MPa |
Yield strength | 23.0 °C | 305 - 353 MPa Show Supplier Material materials with Yield strength of 305 - 353 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2.25E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.25E-5 1/K | Mean values between 20°C and the mentioned temperature |
Specific heat capacity | 23.0 °C | 864 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 864 J/(kg·K) | |
Thermal conductivity | 23.0 °C | 130 W/(m·K) Show Supplier Material materials with Thermal conductivity of 130 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 23.0 °C | 1.74E+7 S/m Show Supplier Material materials with Electrical conductivity of 1.74E+7 S/m |
Chemical properties
Property | Value | Comment | |
---|---|---|---|
Aluminium | Balance | ||
Chromium | 0.05 % Show Supplier Material materials with Chromium of 0.05 % | ||
Copper | 5.8 - 6.8 % Show Supplier Material materials with Copper of 5.8 - 6.8 % | ||
Iron | 0.4 % Show Supplier Material materials with Iron of 0.4 % | ||
Magnesium | 0.1 % Show Supplier Material materials with Magnesium of 0.1 % | ||
Manganese | 0.2 - 0.4 % Show Supplier Material materials with Manganese of 0.2 - 0.4 % | ||
Other | 0.15 % Show Supplier Material materials with Other of 0.15 % | Total | |
Silicon | 0.3 % Show Supplier Material materials with Silicon of 0.3 % | ||
Titanium | 0.02 - 0.1 % Show Supplier Material materials with Titanium of 0.02 - 0.1 % | ||
Zinc | 0.1 % Show Supplier Material materials with Zinc of 0.1 % |
Technological properties
Property | ||
---|---|---|
Anodizing | good | |
Application areas | Tool making, mould making and model making; Blow moulds and injection moulds; Laminating tools; Moulds for elastomer materials; Moulds and heat-stressed parts; Moulds with welded construction; Refrigeration technology | |
Corrosion properties | moderate | |
Dimensional stability | good | |
General machinability | very good | |
Soldering general | not recommended | |
Welding | WIG: good, MIG: good, Resistance welding: good |