Rubalit® 717 porous C

Want to keep this datasheet? Save it now in your required format

Description

Rubalit is a highly dense technical oxide ceramic material that can be determined by characteristics of hardness and high strength in combination with that of temperature stability. High corrosion against and wear resistance defines the material for excellent usage in various chemical applications.

This material data has been provided by CeramTec.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Properties

General

Property	Value	Comment
Density	3 g/cm³ Show Supplier Material materials with Density of 3 g/cm³
Surface roughness	0.4 μm Show Supplier Material materials with Surface roughness of 0.4 μm	as fired surface
Water absorption	6 % Show Supplier Material materials with Water absorption of 6 %

Mechanical

Property	Value	Testing Standard	Comment
Flexural strength	200 MPa Show Supplier Material materials with Flexural strength of 200 MPa	DR sigma 0	1.00 mm thickness \| rings 6 / 12 mm

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion		6.3e-06 - 8.3e-06 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6.3e-06 - 8.3e-06 1/K	100-200°C
		6.4e-06 - 8.4e-06 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6.4e-06 - 8.4e-06 1/K	100-300°C
		6.9e-06 - 8.9e-06 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6.9e-06 - 8.9e-06 1/K	100-600°C
		7.2e-06 - 9.2e-06 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.2e-06 - 9.2e-06 1/K	100-800°C
Thermal conductivity	20 °C	18 W/(m·K) Show Supplier Material materials with Thermal conductivity of 18 W/(m·K)	Xe-flash \| sample 16*16mm² \| material specific thickness ≤ 3.5mm

Technological properties

Property

Chemical composition

The material main component is Al₂O₃ with 98.5% content. Residue mainly consists of MgO, SiO2 and CaO and traces of other elements.

Rubalit® 717 porous C