Al cast plate G.AL® C210R, sawed mould plate

Want to keep this datasheet? Save it now in your required format

Description

A medium-strength aluminum plate, G.AL® C210R is the all-rounder of aluminum materials. The G.AL® C210R sawn on all sides is characterized by extremely low-stress properties, dimensional stability and excellent homogeneity over the entire ingot cross section. Based on alloy EN AW 5083 (AlMg4.5Mn0.7), G.AL® C210R is corrosion-resistant to a large extent and can be technically anodized very well. With an slab thickness of up to 42.1 in. and width up to 85.0 in. large-scale projects can be also be realized.

Equivalent Materials

This material data has been provided by Gleich Aluminum.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

23.0 °C

2.66 g/cm³

Show Supplier Material materials with Density of 2.66 g/cm³

Surface roughness

15 μm

Show Supplier Material materials with Surface roughness of 15 μm

Dimension

PropertyValue

Width

1520 mm

Show Supplier Material materials with Width of 1520 mm

Dimensions

Standard stock sizes: 1520mm x 3020mm, 1570mm x 3670mm, 2160mm x 4000mm and 20-1070mm in thickness

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

70 GPa

Show Supplier Material materials with Elastic modulus of 70 GPa

Elongation A5

23.0 °C

10 - 15 %

Show Supplier Material materials with Elongation A5 of 10 - 15 %

Hardness, HBW

23.0 °C

68 - 75 [-]

Show Supplier Material materials with Hardness, HBW of 68 - 75 [-]

Test method: 2.5/62.5

Tensile strength

23.0 °C

230 - 290 MPa

Show Supplier Material materials with Tensile strength of 230 - 290 MPa

Yield strength Rp0.2

23.0 °C

110 - 130 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 110 - 130 MPa

Thermal

PropertyTemperatureValue

Coefficient of thermal expansion

23.0 °C

2.33E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 2.33E-5 1/K

Specific heat capacity

23.0 °C

900 J/(kg·K)

Show Supplier Material materials with Specific heat capacity of 900 J/(kg·K)

Thermal conductivity

23.0 °C

110 - 130 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 110 - 130 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

23.0 °C

1.60E+7 - 1.80E+7 S/m

Show Supplier Material materials with Electrical conductivity of 1.60E+7 - 1.80E+7 S/m

Technological properties

Property
Other

Non heat treatable

Processing history

Temper: O3, homogenized and stress relieved