Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.02 g/cm³ Show Supplier Material materials with Density of 1.02 g/cm³ | ISO1183 |
Mechanical
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongation | 23.0 °C | 300 % Show Supplier Material materials with Elongation of 300 % | ISO527 | ||
Flexural modulus | 23.0 °C | 0.3 GPa Show Supplier Material materials with Flexural modulus of 0.3 GPa | ISO178 | ||
Flexural strength | 23.0 °C | 15 MPa Show Supplier Material materials with Flexural strength of 15 MPa | ISO178 | ||
Hardness, Shore D | 23.0 °C | 60 - 62 [-] Show Supplier Material materials with Hardness, Shore D of 60 - 62 [-] | ISO868 | ||
Impact strength, Charpy notched | -30.0 °C | 45 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 45 kJ/m² | ISO179 | ||
23.0 °C | 70 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 70 kJ/m² | ISO179 | |||
Tensile strength | 23.0 °C | 48 MPa Show Supplier Material materials with Tensile strength of 48 MPa | ISO527 | ||
Yield strength | 23.0 °C | 21 MPa Show Supplier Material materials with Yield strength of 21 MPa | ISO527 | ||
Impact strength, Charpy unnotched | ISO179, No break @-30, 23°C | ||||
Technological properties
| Property | ||
|---|---|---|
| Application areas | Nylon badmintion, shuttlecock | |
| Processing methods | Drying Temperature: 75-80°C, Drying Time: 3-4 hr, Rear Temperature: 180°C, Middle Temperature: 250°C, Front Temperature: 250°C, Nozzle Temperature: 230°C, Mold Temperature: 60-80°C, Injection Pressure: 70-100 MPa | |