Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.08 g/cm³ Show Supplier Material materials with Density of 1.08 g/cm³ | ISO1183 |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 2.5 GPa Show Supplier Material materials with Elastic modulus of 2.5 GPa | ISO527 |
Elongation | 23.0 °C | 300 % Show Supplier Material materials with Elongation of 300 % | ISO527 |
Impact strength, Charpy notched | -30.0 °C | 6 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO179 |
23.0 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO179 | |
Tensile strength | 23.0 °C | 66 MPa Show Supplier Material materials with Tensile strength of 66 MPa | ISO527 |
Thermal
| Property | Value | Comment |
|---|---|---|
Glass transition temperature | 60 °C Show Supplier Material materials with Glass transition temperature of 60 °C | ISO11357-1 |
Heat deflection temperature, 1.80 MPa | 68 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 68 °C | ISO75/A |
Melting point | 215 °C Show Supplier Material materials with Melting point of 215 °C | ISO11357-1 |
Rheological Properties
| Property | Temperature | Value |
|---|---|---|
Shrinkage | 23.0 °C | 1.3 - 1.4 % Show Supplier Material materials with Shrinkage of 1.3 - 1.4 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Gears, battery cover, toothbrush wire, industrial brush wire | |
| Processing methods | Drying Temperature: 80-85°C, Drying Time: 4-5 hr, Rear Temperature: 215°C, Middle Temperature: 220°C, Front Temperature: 225°C, Nozzle Temperature: 225°C, Mold Temperature: 40-60°C, Injection Pressure: 80-100 MPa | |