PA612 resins H3G30

Alternative and trade names
Dupont 77G33L
Want to keep this datasheet? Save it now in your required format

Description

Low absorption,size stability, excellent low temperature performace

This material data has been provided by Global Star Trading (HK) Co. Ltd.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.28 g/cm³

Show Supplier Material materials with Density of 1.28 g/cm³

ISO1183

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

7 %

Show Supplier Material materials with Elongation of 7 %

ISO527

Flexural modulus

23.0 °C

8 GPa

Show Supplier Material materials with Flexural modulus of 8 GPa

ISO178

Flexural strength

23.0 °C

200 MPa

Show Supplier Material materials with Flexural strength of 200 MPa

ISO178

Impact strength, Charpy notched

-30.0 °C

13 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 13 kJ/m²

ISO179

23.0 °C

18 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 18 kJ/m²

ISO179

Tensile strength

23.0 °C

145 MPa

Show Supplier Material materials with Tensile strength of 145 MPa

ISO527

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

175 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 175 °C

ISO75

Technological properties

Property
Application areas

Automotive lightweight components, Tubing connection, Sport health equipment

Fillers

30% Glass Fiber

Processing methods

Drying Temperature: 80-85°C, Drying Time: 3-4 hr, Rear Temperature: 210°C, Middle Temperature: 220°C, Front Temperature: 230°C, Nozzle Temperature: 220°C, Mold Temperature: 60-80°C, Injection Pressure: 80-100 MPa