General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.37 g/cm³ Show Supplier Material materials with Density of 1.37 g/cm³ | ISO1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 6 % Show Supplier Material materials with Elongation of 6 % | ISO527 |
Flexural modulus | 23.0 °C | 9.5 GPa Show Supplier Material materials with Flexural modulus of 9.5 GPa | ISO178 |
Flexural strength | 23.0 °C | 220 MPa Show Supplier Material materials with Flexural strength of 220 MPa | ISO178 |
Impact strength, Charpy notched | -30.0 °C | 13 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 13 kJ/m² | ISO179 |
23.0 °C | 20 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 20 kJ/m² | ISO179 | |
Tensile strength | 23.0 °C | 160 MPa Show Supplier Material materials with Tensile strength of 160 MPa | ISO527 |
Thermal
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 1.80 MPa | 185 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 185 °C | ISO75 |
Technological properties
Property | ||
---|---|---|
Application areas | Automotive lightweight components, Tubing connection, Sport health equipment | |
Fillers | 40% Glass Fiber | |
Processing methods | Drying Temperature: 80-85°C, Drying Time: 3-4 hr, Rear Temperature: 210°C, Middle Temperature: 220°C, Front Temperature: 230°C, Nozzle Temperature: 220°C, Mold Temperature: 60-80°C, Injection Pressure: 80-100 MPa |