Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.07 g/cm³ Show Supplier Material materials with Density of 1.07 g/cm³ | ISO1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.3 GPa Show Supplier Material materials with Elastic modulus of 2.3 GPa | ISO527 |
Elongation | 23.0 °C | 200 % Show Supplier Material materials with Elongation of 200 % | ISO527 |
Impact strength, Charpy notched | -30.0 °C | 6 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO179 |
23.0 °C | 8 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO179 | |
Tensile strength | 23.0 °C | 62 MPa Show Supplier Material materials with Tensile strength of 62 MPa | ISO527 |
Thermal
Property | Value | Comment |
---|---|---|
Glass transition temperature | 60 °C Show Supplier Material materials with Glass transition temperature of 60 °C | ISO11357-1 |
Heat deflection temperature, 1.80 MPa | 65 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 65 °C | ISO75/A |
Melting point | 210 °C Show Supplier Material materials with Melting point of 210 °C | ISO11357-1 |
Technological properties
Property | ||
---|---|---|
Application areas | Toothbrush wire, industrial brush wire, battery end cap, Gears | |
Processing methods | Drying Temperature: 80-85°C, Drying Time: 4-5 hr, Rear Temperature: 215°C, Middle Temperature: 220°C, Front Temperature: 225°C, Nozzle Temperature: 225°C, Mold Temperature: 60-80°C, Injection Pressure: 80-100 MPa |